Solar cell

A solar cell made from a monocrystalline silicon wafer

A monocrystalline solar cell

A solar cell (also called photovoltaic cell or photoelectric cell) is a solid state electrical device that converts the energy of light directly into electricity by the photovoltaic effect.

Assemblies of cells used to make solar modules which are used to capture energy from sunlight, are known as solar panels. The energy generated from these solar modules, referred to as solar power, is an example of solar energy.

Photovoltaics is the field of technology and research related to the practical application of photovoltaic cells in producing electricity from light, though it is often used specifically to refer to the generation of electricity from sunlight.

Cells are described as photovoltaic cells when the light source is not necessarily sunlight. These are used for detecting light or other electromagnetic radiation near the visible range, for example infrared detectors, or measurement of light intensity.

History of solar cells

Main article: Timeline of solar cells

The term "photovoltaic" comes from the Greek φῶς (phōs) meaning "light", and "voltaic", from the name of the Italian physicist Volta, after whom a unit of electro-motive force, the volt, is named. The term "photo-voltaic" has been in use in English since 1849.^[1]

The photovoltaic effect was first recognized in 1839 by French physicist A. E. Becquerel. However, it was not until 1883 that the first photovoltaic cell was built, by Charles Fritts, who coated the semiconductor selenium with an extremely thin layer of gold to form the junctions. The device was only around 1% efficient. In 1888 Russian physicist Aleksandr Stoletov built the first photoelectric cell based on the outer photoelectric effect discovered by Heinrich Hertz earlier in 1887.

Albert Einstein explained the photoelectric effect in 1905 for which he received the Nobel prize in Physics in 1921.^[2] Russell Ohl patented the modern junction semiconductor solar cell in 1946,^[3] which was discovered while working on the series of advances that would lead to the transistor.

Bell produces the first practical cell

The modern photovoltaic cell was developed in 1954 at Bell Laboratories.^[4] The highly efficient solar cell was first developed by Daryl Chapin, Calvin Souther Fuller and Gerald Pearson in 1954 using a diffused silicon p-n junction.^[5] At first, cells were developed for toys and other minor uses, as the cost of the electricity they produced was very high; in relative terms, a cell that produced 1 watt of electrical power in bright sunlight cost about $250, comparing to $2 to $3 for a coal plant.

Solar cells were rescued from obscurity by the suggestion to add them to the Vanguard I satellite, launched in 1958. In the original plans, the satellite would be powered only by battery, and last a short time while this ran down. By adding cells to the outside of the body, the mission time could be extended with no major changes to the spacecraft or its power systems. There was some scepticism at first, but in practice the cells proved to be a huge success, and solar cells were quickly designed into many new satellites, notably Bell's own Telstar.

Improvements were slow over the next two decades, and the only widespread use was in space applications where their power-to-weight ratio was higher than any competing technology. However, this success was also the reason for slow progress; space users were willing to pay anything for the best possible cells, there was no reason to invest in lower-cost solutions if this would reduce efficiency. Instead, the price of cells was determined largely by the semiconductor industry; their move to integrated circuits in the 1960s led to the availability of larger boules at lower relative prices. As their price fell, the price of the resulting cells did as well. However these effects were limited, and by 1971 cell costs were estimated to be $100 per watt.^[6]

Berman's price reductions

In the late 1960s, Elliot Berman was investigating a new method for producing the silicon feedstock in a ribbon process. However, he found little interest in the project and was unable to gain the funding needed to develop it. In a chance encounter, he was later introduced to a team at Exxon who were looking for projects 30 years in the future. The group had concluded that electrical power would be much more expensive by 2000, and felt that this increase in price would make new alternative energy sources more attractive, and solar was the most interesting among these. In 1969, Berman joined the Linden, New Jersey Exxon lab, Solar Power Corporation (SPC).^[7]

His first major effort was to canvas the potential market to see what possible uses for a new product were, and they quickly found that if the price per watt were reduced from then-current $100/watt to about $20/watt there would be significant demand. Knowing that his ribbon concept would take years to develop, the team started looking for ways to hit the $20 price point using existing materials.^[7]

The first improvement was the realization that the existing cells were based on standard semiconductor manufacturing process, even though that was not ideal. This started with the boule, cutting it into disks called wafers, polishing the wafers, and then, for cell use, coating them with an anti-reflective layer. Berman noted that the rough-sawn wafers already had a perfectly suitable anti-reflective front surface, and by printing the electrodes directly on this surface, two major steps in the cell processing were eliminated. The team also explored ways to improve the mounting of the cells into arrays, eliminating the expensive materials and hand wiring used in space applications. Their solution was to use a printed circuit board on the back, acrylic plastic on the front, and silicone glue between the two, potting the cells. The largest improvement in price point was Berman's realization that existing silicon was effectively "too good" for solar cell use; the minor imperfections that would ruin a boule (or individual wafer) for electronics would have little effect in the solar application.^[8] Solar cells could be made using cast-off material from the electronics market.

Putting all of these changes into practice, the company started buying up "reject" silicon from existing manufacturers at very low cost. By using the largest wafers available, thereby reducing the amount of wiring for a given panel area, and packaging them into panels using their new methods, by 1973 SPC was producing panels at $10 per watt and selling them at $20 per watt, a fivefold decrease in prices in two years.

Navigation market

SPC approached companies making navigational buoys as a natural market for their products, but found a curious situation. The primary company in the business was Automatic Power, a battery manufacturer. Realizing that solar cells might eat into their battery profits, Automatic purchased the rights to earlier solar cell designs and suppressed them.^{[citation needed]} Seeing there was no interest at Automatic Power, SPC turned to Tideland Signal, another battery company formed by ex-Automatic managers. Tideland introduced a solar-powered buoy and was soon ruining Automatic's business.

The timing could not be better; the rapid increase in the number of offshore oil platforms and loading facilities produced an enormous market among the oil companies. As Tideland's fortunes improved, Automatic Power started looking for their own supply of solar panels. They found Bill Yerks of Solar Power International (SPI) in California, who was looking for a market. SPI was soon bought out by one of its largest customers, the ARCO oil giant, forming ARCO Solar. ARCO Solar's factory in Camarillo, California was the first dedicated to building solar panels, and has been in continual operation from its purchase by ARCO in 1977 to this day.

This market, combined with the 1973 oil crisis, led to a curious situation. Oil companies were now cash-flush due to their huge profits during the crisis, but were also acutely aware that their future success would depend on some other form of power. Over the next few years, major oil companies started a number of solar firms, and were for decades the largest producers of solar panels. Exxon, ARCO, Shell, Amoco (later purchased by BP) and Mobil all had major solar divisions during the 1970s and 1980s. Technology companies also had some investment, including General Electric, Motorola, IBM, Tyco and RCA.^[9]

Further improvements

In the time since Berman's work, improvements have brought production costs down under $1 a watt, with wholesale costs on the order of $2. "Balance of system" costs are now more than the panels themselves. Large commercial arrays can be built at below $3.40 a watt,^[10][11] fully commissioned.

As the semiconductor industry moved to ever-larger boules, older equipment became available at fire-sale prices. Cells have grown in size as older equipment became available on the surplus market; ARCO Solar's original panels used cells with 2 to 4 inch (51 to 100 mm) diameter. Panels in the 1990s and early 2000s generally used 5 inch (125 mm) wafers, and since 2008 almost all new panels use 6 inch (150 mm) cells. Another major change was the move to polycrystalline silicon. This material has less efficiency, but is less expensive to produce in bulk. The widespread introduction of flat screen televisions in the late 1990s and early 2000s led to the wide availability of large sheets of high-quality glass, used on the front of the panels.

Current events

Other technologies have tried to enter the market. First Solar was briefly the largest panel manufacturer in 2009, in terms of yearly power produced, using a thin-film cell sandwiched between two layers of glass. Since then Silicon panels reasserted their dominant position both in terms of lower prices and the rapid rise of Chinese manufacturing, resulting in the top producers being Chinese. By late 2011, efficient production in China, coupled with a drop in European demand due to budgetary turmoil had dropped prices for crystalline solar-based modules further, to about $1.09^[11] per watt in October 2011, down sharply from from the price per watt in 2010.

Applications

Polycrystalline photovoltaic cells laminated to backing material in a module

Polycrystalline photovoltaic cells

Main article: photovoltaic system

Solar cells are often electrically connected and encapsulated as a module. Photovoltaic modules often have a sheet of glass on the front (sun up) side, allowing light to pass while protecting the semiconductor wafers from abrasion and impact due to wind-driven debris, rain, hail, etc. Solar cells are also usually connected in series in modules, creating an additive voltage. Connecting cells in parallel will yield a higher current; however, very significant problems exist with parallel connections. For example, shadow effects can shut down the weaker (less illuminated) parallel string (a number of series connected cells) causing substantial power loss and even damaging excessive reverse bias applied to the shadowed cells by their illuminated partners. As far as possible, strings of series cells should be handled independently and not connected in parallel, save using special paralleling circuits. Although modules can be interconnected in series and/or parallel to create an array with the desired peak DC voltage and loading current capacity, using independent MPPTs (maximum power point trackers) provides a better solution. In the absence of paralleling circuits, shunt diodes can be used to reduce the power loss due to shadowing in arrays with series/parallel connected cells.

To make practical use of the solar-generated energy, the electricity is most often fed into the electricity grid using inverters (grid-connected photovoltaic systems); in stand-alone systems, batteries are used to store the energy that is not needed immediately. Solar panels can be used to power or recharge portable devices.

Theory

Main article: Theory of solar cells

The solar cell works in three steps:

1. Photons in sunlight hit the solar panel and are absorbed by semiconducting materials, such as silicon.
2. Electrons (negatively charged) are knocked loose from their atoms, causing an electric potential difference. Current starts flowing through the material to cancel the potential and this electricity is captured. Due to the special composition of solar cells, the electrons are only allowed to move in a single direction.
3. An array of solar cells converts solar energy into a usable amount of direct current (DC) electricity.

Efficiency

Main article: Solar cell efficiency

The efficiency of a solar cell may be broken down into reflectance efficiency, thermodynamic efficiency, charge carrier separation efficiency and conductive efficiency. The overall efficiency is the product of each of these individual efficiencies.

Due to the difficulty in measuring these parameters directly, other parameters are measured instead: thermodynamic efficiency, quantum efficiency, integrated quantum efficiency, V_OC ratio, and fill factor. Reflectance losses are a portion of the quantum efficiency under "external quantum efficiency". Recombination losses make up a portion of the quantum efficiency, V_OC ratio, and fill factor. Resistive losses are predominantly categorized under fill factor, but also make up minor portions of the quantum efficiency, V_OC ratio.

The fill factor is defined as the ratio of the actual maximum obtainable power, to the product of the open circuit voltage and short circuit current. This is a key parameter in evaluating the performance of solar cells. Typical commercial solar cells have a fill factor > 0.70. Grade B cells have a fill factor usually between 0.4 to 0.7. The fill factor is, besides efficiency, one of the most significant parameters for the energy yield of a photovoltaic cell.^[12] Cells with a high fill factor have a low equivalent series resistance and a high equivalent shunt resistance, so less of the current produced by light is dissipated in internal losses.

Single p-n junction crystalline silicon devices are now approaching the theoretical limiting efficiency of 37.7% as stated by Shockley-Quissler in 1961. However multiple layer solar cells have a theoretical limit of 86%.

Cost

The cost of a solar cell is given per unit of peak electrical power. Manufacturing costs necessarily include the cost of energy required for manufacture. Solar-specific feed in tariffs vary worldwide, and even state by state within various countries.^[13] Such feed-in tariffs can be highly effective in encouraging the development of solar power projects.

High-efficiency solar cells are of interest to decrease the cost of solar energy. Many of the costs of a solar power plant are proportional to the area of the plant; a higher efficiency cell may reduce area and plant cost, even if the cells themselves are more costly. Efficiencies of bare cells, to be useful in evaluating solar power plant economics, must be evaluated under realistic conditions. The basic parameters that need to be evaluated are the short circuit current, open circuit voltage.^[14]

The chart below illustrates the best laboratory efficiencies obtained for various materials and technologies, generally this is done on very small, i.e., one square cm, cells. Commercial efficiencies are significantly lower.

Reported timeline of solar cell energy conversion efficiencies (from National Renewable Energy Laboratory (USA)

Grid parity, the point at which photovoltaic electricity is equal to or cheaper than grid power, can be reached using low cost solar cells. It is achieved first in areas with abundant sun and high costs for electricity such as in California and Japan.^[15] Grid parity has been reached in Hawaii and other islands that otherwise use diesel fuel to produce electricity. George W. Bush had set 2015 as the date for grid parity in the USA.^[16][17] Speaking at a conference in 2007, General Electric's Chief Engineer predicted grid parity without subsidies in sunny parts of the United States by around 2015.^[18]

The price of solar panels fell steadily for 40 years, until 2004 when high subsidies in Germany drastically increased demand there and greatly increased the price of purified silicon (which is used in computer chips as well as solar panels). The great recession of 2008, and the onset of Chinese manufacturing, caused prices to resume their decline with vehemence. In the four years after January 2008 spot prices for solar modules in the German market prices dropped from €3 to €1 per Watt peak. During that same times production capacity surged with an annual growth of more than 50% and the Mainland Chinese went from single digit to over 50% market share.^[19]

Materials

The Shockley-Queisser limit for the theoretical maximum efficiency of a solar cell. Semiconductors with band gap between 1 and 1.5eV have the greatest potential to form an efficient cell. (The efficiency "limit" shown here can be exceeded by multijunction solar cells.)

Different materials display different efficiencies and have different costs. Materials for efficient solar cells must have characteristics matched to the spectrum of available light. Some cells are designed to efficiently convert wavelengths of solar light that reach the Earth surface. However, some solar cells are optimized for light absorption beyond Earth's atmosphere as well. Light absorbing materials can often be used in multiple physical configurations to take advantage of different light absorption and charge separation mechanisms.

Materials presently used for photovoltaic solar cells include monocrystalline silicon, polycrystalline silicon, amorphous silicon, cadmium telluride, and copper indium selenide/sulfide.^[20]

Many currently available solar cells are made from bulk materials that are cut into wafers between 180 to 240 micrometers thick that are then processed like other semiconductors.

Other materials are made as thin-films layers, organic dyes, and organic polymers that are deposited on supporting substrates. A third group are made from nanocrystals and used as quantum dots (electron-confined nanoparticles). Silicon remains the only material that is well-researched in both bulk and thin-film forms.

Crystalline silicon

Main articles: Monocrystalline silicon, Polycrystalline silicon, Silicon, and list of silicon producers

Basic structure of a silicon based solar cell and its working mechanism.

By far, the most prevalent bulk material for solar cells is crystalline silicon (abbreviated as a group as c-Si), also known as "solar grade silicon". Bulk silicon is separated into multiple categories according to crystallinity and crystal size in the resulting ingot, ribbon, or wafer.

1. monocrystalline silicon (c-Si): often made using the Czochralski process. Single-crystal wafer cells tend to be expensive, and because they are cut from cylindrical ingots, do not completely cover a square solar cell module without a substantial waste of refined silicon. Hence most c-Si panels have uncovered gaps at the four corners of the cells.
2. polycrystalline silicon, or multicrystalline silicon, (poly-Si or mc-Si): made from cast square ingots — large blocks of molten silicon carefully cooled and solidified. Poly-Si cells are less expensive to produce than single crystal silicon cells, but are less efficient. United States Department of Energy data show that there were a higher number of polycrystalline sales than monocrystalline silicon sales.
3. ribbon silicon^[21] is a type of polycrystalline silicon: it is formed by drawing flat thin films from molten silicon and results in a polycrystalline structure. These cells have lower efficiencies than poly-Si, but save on production costs due to a great reduction in silicon waste, as this approach does not require sawing from ingots.

Analysts have predicted that prices of polycrystalline silicon will drop as companies build additional polysilicon capacity quicker than the industry's projected demand. On the other hand, the cost of producing upgraded metallurgical-grade silicon, also known as UMG Si, can potentially be one-sixth that of making polysilicon.^[22]

Manufacturers of wafer-based cells have responded to high silicon prices in 2004-2008 prices with rapid reductions in silicon consumption. According to Jef Poortmans, director of IMEC's organic and solar department, current cells use between eight and nine grams of silicon per watt of power generation, with wafer thicknesses in the neighborhood of 0.200 mm. At 2008 spring's IEEE Photovoltaic Specialists' Conference (PVS'08), John Wohlgemuth, staff scientist at BP Solar, reported that his company has qualified modules based on 0.180 mm thick wafers and is testing processes for 0.16 mm wafers cut with 0.1 mm wire. IMEC's road map, presented at the organization's recent annual research review meeting, envisions use of 0.08 mm wafers by 2015.^[23]

Thin films

Main article: Thin film solar cell

Market share of the different PV technologies In 2010 the market share of thin film declined by 30% as thin film technology was displaced by more efficient crystalline silicon solar panels (the light and dark blue bars).

Thin-film technologies reduce the amount of material required in creating the active material of solar cell. Most thin film solar cells are sandwiched between two panes of glass to make a module. Since silicon solar panels only use one pane of glass, thin film panels are approximately twice as heavy as crystalline silicon panels. The majority of film panels have significantly lower conversion efficiencies, lagging silicon by two to three percentage points.^[24] Thin-film solar technologies have enjoyed large investment due to the success of First Solar and the largely unfulfilled promise of lower cost and flexibility compared to wafer silicon cells, but they have not become mainstream solar products due to their lower efficiency and corresponding larger area consumption per watt production. Cadmium telluride (CdTe), copper indium gallium selenide (CIGS) and amorphous silicon (A-Si) are three thin-film technologies often used as outdoor photovoltaic solar power production. CdTe technology is most cost competitive among them.^[25] CdTe technology costs about 30% less than CIGS technology and 40% less than A-Si technology in 2011.

Cadmium telluride solar cell

Main article: Cadmium telluride photovoltaics

A cadmium telluride solar cell uses a cadmium telluride (CdTe) thin film, a semiconductor layer to absorb and convert sunlight into electricity. Solarbuzz^[26] has reported that the lowest quoted thin-film module price stands at US$1.76 per watt-peak, with the lowest crystalline silicon (c-Si) module at $2.48 per watt-peak.

The cadmium present in the cells would be toxic if released. However, release is impossible during normal operation of the cells and is unlikely during fires in residential roofs.^[27] A square meter of CdTe contains approximately the same amount of Cd as a single C cell Nickel-cadmium battery, in a more stable and less soluble form.^[27]

Copper indium gallium selenide

Main article: Copper indium gallium selenide solar cell

Copper indium gallium selenide (CIGS) is a direct band gap material. It has the highest efficiency (~20%) among thin film materials (see CIGS solar cell). Traditional methods of fabrication involve vacuum processes including co-evaporation and sputtering. Recent developments at IBM and Nanosolar attempt to lower the cost by using non-vacuum solution processes.

Gallium arsenide multijunction

Main article: Multijunction photovoltaic cell

High-efficiency multijunction cells were originally developed for special applications such as satellites and space exploration, but at present, their use in terrestrial concentrators might be the lowest cost alternative in terms of $/kWh and $/W.^[28] These multijunction cells consist of multiple thin films produced using metalorganic vapour phase epitaxy. A triple-junction cell, for example, may consist of the semiconductors: GaAs, Ge, and GaInP₂.^[29] Each type of semiconductor will have a characteristic band gap energy which, loosely speaking, causes it to absorb light most efficiently at a certain color, or more precisely, to absorb electromagnetic radiation over a portion of the spectrum. The semiconductors are carefully chosen to absorb nearly all of the solar spectrum, thus generating electricity from as much of the solar energy as possible.

GaAs based multijunction devices are the most efficient solar cells to date. In October 2010, triple junction metamorphic cell reached a record high of 42.3%.^[30] This technology is currently being utilized in the Mars Exploration Rover missions, which have run far past their 90 day design life.

Tandem solar cells based on monolithic, series connected, gallium indium phosphide (GaInP), gallium arsenide GaAs, and germanium Ge p-n junctions, are seeing demand rapidly rise. Between December 2006 and December 2007, the cost of 4N gallium metal rose from about $350 per kg to $680 per kg. Additionally, germanium metal prices have risen substantially to $1000–$1200 per kg this year. Those materials include gallium (4N, 6N and 7N Ga), arsenic (4N, 6N and 7N) and germanium, pyrolitic boron nitride (pBN) crucibles for growing crystals, and boron oxide, these products are critical to the entire substrate manufacturing industry.

Triple-junction GaAs solar cells were also being used as the power source of the Dutch four-time World Solar Challenge winners Nuna in 2003, 2005 and 2007, and also by the Dutch solar cars Solutra (2005), Twente One (2007) and 21Revolution (2009).

The Dutch Radboud University Nijmegen set the record for thin film solar cell efficiency using a single junction GaAs to 25.8% in August 2008 using only 4 µm thick GaAs layer which can be transferred from a wafer base to glass or plastic film.^[31]

Light-absorbing dyes (DSSC)

Main article: Dye-sensitized solar cells

Dye-sensitized solar cells (DSSCs) are made of low-cost materials and do not need elaborate equipment to manufacture, so they can be made in a DIY fashion, possibly allowing players to produce more of this type of solar cell than others. In bulk it should be significantly less expensive than older solid-state cell designs. DSSC's can be engineered into flexible sheets, and although its conversion efficiency is less than the best thin film cells, its price/performance ratio should be high enough to allow them to compete with fossil fuel electrical generation. The DSSC has been developed by Prof. Michael Grätzel in 1991 at the Swiss Federal Institute of Technology (EPFL) in Lausanne (CH).

Typically a ruthenium metalorganic dye (Ru-centered) is used as a monolayer of light-absorbing material. The dye-sensitized solar cell depends on a mesoporous layer of nanoparticulate titanium dioxide to greatly amplify the surface area (200–300 m²/g TiO₂, as compared to approximately 10 m²/g of flat single crystal). The photogenerated electrons from the light absorbing dye are passed on to the n-type TiO₂, and the holes are absorbed by an electrolyte on the other side of the dye. The circuit is completed by a redox couple in the electrolyte, which can be liquid or solid. This type of cell allows a more flexible use of materials, and is typically manufactured by screen printing and/or use of Ultrasonic Nozzles, with the potential for lower processing costs than those used for bulk solar cells. However, the dyes in these cells also suffer from degradation under heat and UV light, and the cell casing is difficult to seal due to the solvents used in assembly. In spite of the above, this is a popular emerging technology with some commercial impact forecast within this decade. The first commercial shipment of DSSC solar modules occurred in July 2009 from G24i Innovations.^[32]

Organic/polymer solar cells

Organic solar cells are a relatively novel technology, yet hold the promise of a substantial price reduction (over thin-film silicon) and a faster return on investment. These cells can be processed from solution, hence the possibility of a simple roll-to-roll printing process, leading to inexpensive, large scale production.

Organic solar cells and polymer solar cells are built from thin films (typically 100 nm) of organic semiconductors including polymers, such as polyphenylene vinylene and small-molecule compounds like copper phthalocyanine (a blue or green organic pigment) and carbon fullerenes and fullerene derivatives such as PCBM. Energy conversion efficiencies achieved to date using conductive polymers are low compared to inorganic materials. However, it has improved quickly in the last few years and the highest NREL (National Renewable Energy Laboratory) certified efficiency has reached 8.3% for the Konarka Power Plastic.^[33] In addition, these cells could be beneficial for some applications where mechanical flexibility and disposability are important.

These devices differ from inorganic semiconductor solar cells in that they do not rely on the large built-in electric field of a PN junction to separate the electrons and holes created when photons are absorbed. The active region of an organic device consists of two materials, one which acts as an electron donor and the other as an acceptor. When a photon is converted into an electron hole pair, typically in the donor material, the charges tend to remain bound in the form of an exciton, and are separated when the exciton diffuses to the donor-acceptor interface. The short exciton diffusion lengths of most polymer systems tend to limit the efficiency of such devices. Nanostructured interfaces, sometimes in the form of bulk heterojunctions, can improve performance.^[34]

Silicon thin films

Silicon thin-film cells are mainly deposited by chemical vapor deposition (typically plasma-enhanced, PE-CVD) from silane gas and hydrogen gas. Depending on the deposition parameters, this can yield:^[35]

1. Amorphous silicon (a-Si or a-Si:H)
2. Protocrystalline silicon or
3. Nanocrystalline silicon (nc-Si or nc-Si:H), also called microcrystalline silicon.

It has been found that protocrystalline silicon with a low volume fraction of nanocrystalline silicon is optimal for high open circuit voltage.^[36] These types of silicon present dangling and twisted bonds, which results in deep defects (energy levels in the bandgap) as well as deformation of the valence and conduction bands (band tails). The solar cells made from these materials tend to have lower energy conversion efficiency than bulk silicon, but are also less expensive to produce. The quantum efficiency of thin film solar cells is also lower due to reduced number of collected charge carriers per incident photon.

An amorphous silicon (a-Si) solar cell is made of amorphous or microcrystalline silicon and its basic electronic structure is the p-i-n junction. a-Si is attractive as a solar cell material because it is abundant and non-toxic (unlike its CdTe counterpart) and requires a low processing temperature, enabling production of devices to occur on flexible and low-cost substrates. As the amorphous structure has a higher absorption rate of light than crystalline cells, the complete light spectrum can be absorbed with a very thin layer of photo-electrically active material. A film only 1 micron thick can absorb 90% of the usable solar energy.^[37] This reduced material requirement along with current technologies being capable of large-area deposition of a-Si, the scalability of this type of cell is high. However, because it is amorphous, it has high inherent disorder and dangling bonds, making it a bad conductor for charge carriers. These dangling bonds act as recombination centers that severely reduce the carrier lifetime and pin the Fermi energy level so that doping the material to n- or p- type is not possible. Amorphous Silicon also suffers from the Staebler-Wronski effect, which results in the efficiency of devices utilizing amorphous silicon dropping as the cell is exposed to light. The production of a-Si thin film solar cells uses glass as a substrate and deposits a very thin layer of silicon by plasma-enhanced chemical vapor deposition (PECVD). A-Si manufacturers are working towards lower costs per watt and higher conversion efficiency with continuous research and development on Multijunction solar cells for solar panels. Anwell Technologies Limited recently announced its target for multi-substrate-multi-chamber PECVD, to lower the cost to US$0.5 per watt.^[38]

Amorphous silicon has a higher bandgap (1.7 eV) than crystalline silicon (c-Si) (1.1 eV), which means it absorbs the visible part of the solar spectrum more strongly than the infrared portion of the spectrum. As nc-Si has about the same bandgap as c-Si, the nc-Si and a-Si can advantageously be combined in thin layers, creating a layered cell called a tandem cell. The top cell in a-Si absorbs the visible light and leaves the infrared part of the spectrum for the bottom cell in nc-Si.

Recently, solutions to overcome the limitations of thin-film crystalline silicon have been developed. Light trapping schemes where the weakly absorbed long wavelength light is obliquely coupled into the silicon and traverses the film several times can significantly enhance the absorption of sunlight in the thin silicon films.^[39] Minimizing the top contact coverage of the cell surface is another method for reducing optical losses; this approach simply aims at reducing the area that is covered over the cell to allow for maximum light input into the cell. Anti-reflective coatings can also be applied to create destructive interference within the cell. This can by done by modulating the Refractive index of the surface coating; if destructive interference is achieved, there will be no reflective wave and thus all light will be transmitted into the semiconductor cell. Surface texturing is another option, but may be less viable because it also increases the manufacturing price. By applying a texture to the surface of the solar cell, the reflected light can be refracted into striking the surface again, thus reducing the overall light reflected out. Light trapping as another method allows for a decrease in overall thickness of the device; the path length that the light will travel is several times the actual device thickness. This can be achieved by adding a textured backreflector to the device as well as texturing the surface. If both front and rear surfaces of the device meet this criterion, the light will be 'trapped' by not having an immediate pathway out of the device due to internal reflections. Thermal processing techniques can significantly enhance the crystal quality of the silicon and thereby lead to higher efficiencies of the final solar cells.^[40] Further advancement into geometric considerations of building devices can exploit the dimensionality of nanomaterials. Creating large, parallel nanowire arrays enables long absorption lengths along the length of the wire while still maintaining short minority carrier diffusion lengths along the radial direction. Adding nanoparticles between the nanowires will allow for conduction through the device. Because of the natural geometry of these arrays, a textured surface will naturally form which allows for even more light to be trapped. A further advantage of this geometry is that these types of devices require about 100 times less material than conventional wafer-based devices.

Manufacture

Early calculator solar battery

Because solar cells are semiconductor devices, they share some of the same processing and manufacturing techniques as other semiconductor devices such as computer and memory chips. However, the stringent requirements for cleanliness and quality control of semiconductor fabrication are more relaxed for solar cells. Most large-scale commercial solar cell factories today make screen printed poly-crystalline or single crystalline silicon solar cells.

Poly-crystalline silicon wafers are made by wire-sawing block-cast silicon ingots into very thin (180 to 350 micrometer) slices or wafers. The wafers are usually lightly p-type doped. To make a solar cell from the wafer, a surface diffusion of n-type dopants is performed on the front side of the wafer. This forms a p-n junction a few hundred nanometers below the surface.

Anti-reflection coatings, to increase the amount of light coupled into the solar cell, are typically next applied. Silicon nitride has gradually replaced titanium dioxide as the anti-reflection coating, because of its excellent surface passivation qualities. It prevents carrier recombination at the surface of the solar cell. It is typically applied in a layer several hundred nanometers thick using plasma-enhanced chemical vapor deposition (PECVD). Some solar cells have textured front surfaces that, like anti-reflection coatings, serve to increase the amount of light coupled into the cell. Such surfaces can usually only be formed on single-crystal silicon, though in recent years methods of forming them on multicrystalline silicon have been developed.

The wafer then has a full area metal contact made on the back surface, and a grid-like metal contact made up of fine "fingers" and larger "bus bars" are screen-printed onto the front surface using a silver paste. The rear contact is also formed by screen-printing a metal paste, typically aluminium. Usually this contact covers the entire rear side of the cell, though in some cell designs it is printed in a grid pattern. The paste is then fired at several hundred degrees Celsius to form metal electrodes in ohmic contact with the silicon. Some companies use an additional electro-plating step to increase the cell efficiency. After the metal contacts are made, the solar cells are interconnected in series (and/or parallel) by flat wires or metal ribbons, and assembled into modules or "solar panels". Solar panels have a sheet of tempered glass on the front, and a polymer encapsulation on the back.

Lifespan

Most commercially available solar panels are capable of producing electricity for at least twenty years.^{[citation needed]} The typical warranty given by panel manufacturers is over 90% of rated output for the first 10 years, and over 80% for the second 10 years.^{[citation needed]} Panels are expected to function for a period of 30 to 35 years.^{[citation needed]}

Research topics

Main article: Solar cell research

There are currently many research groups active in the field of photovoltaics in universities and research institutions around the world. This research can be divided into three areas: making current technology solar cells cheaper and/or more efficient to effectively compete with other energy sources; developing new technologies based on new solar cell architectural designs; and developing new materials to serve as light absorbers and charge carriers.

Manufacturers and certification

National Renewable Energy Laboratory tests and validates solar technologies. There are three reliable certifications of solar equipment: UL and IEEE (both U.S. standards) and IEC.

Solar cells are manufactured primarily in Japan, Germany, mainland China, Taiwan and the United States,^[41] though numerous other nations have or are acquiring significant solar cell production capacity. While technologies are constantly evolving toward higher efficiencies, the most effective cells for low cost electrical production are not necessarily those with the highest efficiency, but those with a balance between low-cost production and efficiency high enough to minimize area-related balance of systems cost. Those companies with large scale manufacturing technology for coating inexpensive substrates may, in fact, ultimately be the lowest cost net electricity producers, even with cell efficiencies that are lower than those of single-crystal technologies.

China

Chinese companies have played an important role in solar panels manufacturing in recent years. China produced solar cells/modules with an output of 13 GW in 2010 which represents about half of the global production and makes China the largest producer in the world.^[42] Some Chinese companies such as Suntech Power, Yingli, LDK Solar Co, JA Solar and ReneSola have already announced projects in cooperation with regional governments with hundreds of megawatts each after the "Golden Sun" incentive program was announced by the government.^[43]

United States

Main article: Photovoltaics in the United States

New manufacturing facilities for solar cells and modules in Massachusetts, Michigan, New York, Ohio, Oregon, and Texas promise to add enough capacity to produce thousands of megawatts of solar devices per year within the next few years from 2008.^[44]

In late September 2008, Sanyo Electric Company, Ltd. announced its decision to build a manufacturing plant for solar ingots and wafers in Salem, Oregon. The plant began operating in October 2009 and reached its full production capacity of 70 megawatts (MW) of solar wafers per year in April 2010.

In early October 2008, First Solar, Inc. broke ground on an expansion of its Perrysburg, Ohio, facility that will add enough capacity to produce another 57 MW per year of solar modules at the facility, bringing its total capacity to roughly 192 MW per year. The company expects to complete construction early next year and reach full production by mid-2010.

In mid-October 2008, SolarWorld AG opened a manufacturing plant in Hillsboro, Oregon, that is producing 500 MW of solar cells per year as of 2011.

Solyndra had a manufacturing facility for its unique tubular CIGS technology in California. Solyndra closed its factory on August 31, 2011 and announced it would file for bankruptcy.^[45]

In March 2010, SpectraWatt, Inc. began production at its manufacturing plant in Hopewell Junction, NY, which was expected to produce 120 MW of solar cells per year when it reached full production in 2011. However, the closure of this plant was announced in late 2010 due to deteriorating market conditions coupled with demand drops from Europe.^[46] SpectraWatt filed for bankruptcy on August 24, 2011.^[47]

See also

Anomalous photovoltaic effect Autonomous building Black silicon Energy development Electromotive force (Solar cell) Flexible substrate Green technology List of solar cell manufacturers Metallurgical grade silicon Microgeneration Maximum power point tracking Multijunction solar cell Nanoflake Photovoltaics P-N junction Plasmonic solar cell Printed electronics

Energy portal Renewable energy portal Sustainable development portal Quantum efficiency Quantum efficiency of a solar cell Renewable energy Roll-to-roll processing Shockley-Queisser limit Solar module quality assurance Solar roof Solar shingles Solar tracker Spectrophotometry Silicon thin-film cell Theory of solar cell Thermophotovoltaics Thin film solar cell

References

1. ^ Alfred Smee (1849). Elements of electro-biology,: or the voltaic mechanism of man; of electro-pathology, especially of the nervous system; and of electro-therapeutics. London: Longman, Brown, Green, and Longmans. p. 15. http://books.google.com/?id=CU0EAAAAQAAJ&pg=PA15. 
2. ^ "The Nobel Prize in Physics 1921: Albert Einstein", Nobel Price official page
3. ^ "Light sensitive device" U.S. Patent 2,402,662 Issue date: June 1946
4. ^ K. A. Tsokos, "Physics for the IB Diploma", Fifth edition, Cambridge University Press, Cambridge, 2008, ISBN 0521708206
5. ^ Perlin, John (2004). "The Silicon Solar Cell Turns 50". National Renewable Energy Laboratory. http://www.nrel.gov/docs/fy04osti/33947.pdf. Retrieved 5 October 2010. 
6. ^ John Perlin, "From Space to Earth: The Story of Solar Electricity", Harvard University Press, 2002, pg. 50
7. ^ ^{a b} Perlin, John. From Space to Earth: The Story of Solar Electricity. Harvard University Press, 2002, pg. 53
8. ^ John Perlin, "From Space to Earth: The Story of Solar Electricity", Harvard University Press, 2002, pg. 54
9. ^ The multinational connections-who does what where", New Scientist, 18 October 1979, pg. 177
10. ^ $1/W Photovoltaic Systems DOE whitepaper August 2010
11. ^ ^{a b} http://247wallst.com/2011/10/06/solar-stocks-does-the-punishment-fit-the-crime-fslr-spwra-stp-jaso-tsl-ldk-tan/
12. ^ "T.Bazouni: What is the Fill Factor of a Solar Panel". http://www.solarfreaks.com/what-is-the-fill-factor-of-a-solar-panel-t138.html. Retrieved 2009-02-17. 
13. ^ Solar Feed in Tariffs. Solarfeedintariff.net. Retrieved on 2011-01-19.
14. ^ N. Gupta, G. F. Alapatt, R. Podila, R. Singh, K.F. Poole, (2009). "Prospects of Nanostructure-Based Solar Cells for Manufacturing Future Generations of Photovoltaic Modules". International Journal of Photoenergy 2009: 1. doi:10.1155/2009/154059. 
15. ^ BP Global – Reports and publications – Going for grid parity. Bp.com. Retrieved on 2011-01-19.
16. ^ BP Global – Reports and publications – Gaining on the grid. Bp.com. Retrieved on 2011-01-19.
17. ^ The Path to Grid Parity (Graphic)
18. ^ Wynn, Gerard (2007-10-19). "Solar power edges towards boom time". Reuters. http://www.reuters.com/article/environmentNews/idUSL1878986220071019. Retrieved 2009-07-29. 
19. ^ Monthly statistics in Photon International
20. ^ Mark Z. Jacobson (2009). Review of Solutions to Global Warming, Air Pollution, and Energy Security p. 4.
21. ^ "String ribbon silicon solar cells with 17.8% efficiency". http://www.ece.gatech.edu/research/UCEP/papers/3world/STRING%20RIBBON%20SILICON%20SOLAR%20CELLS%20WITH%2017.8%25%20EFFICIENCY.pdf. 
22. ^ Charting a Path to Low-Cost Solar. Greentech Media (2008-07-16). Retrieved on 2011-01-19.
23. ^ Katherine Derbyshire (January 9, 2009). "Wafer-based Solar Cells Aren't Done Yet". http://www.renewableenergyworld.com/rea/news/story?id=54443. 
24. ^ Datasheets of the market leaders: First Solar for thin film, Suntech and SunPower for crystalline silicon
25. ^ "Thin-Film Cost Reports". pvinsights.com. 2011 [last update]. http://pvinsights.com/Report/ReportPM.php. Retrieved June 19, 2011. 
26. ^ Solar Energy Industry Research and Consultancy. Solarbuzz. Retrieved on 2011-01-19.
27. ^ ^{a b} Fthenakis, Vasilis M. (August 2004). "Life cycle impact analysis of cadmium in CdTe PV production" (PDF). Renewable and Sustainable Energy Reviews 8 (4): 303–334. doi:10.1016/j.rser.2003.12.001. http://www.firstsolar.com/pdf/Brookhaven_Life_Cycle_Analysis.pdf. 
28. ^ Swanson, R. M. (2000). "The Promise of Concentrators". Progress in Photovoltaics: Res. Appl. 8 (1): 93–111. doi:10.1002/(SICI)1099-159X(200001/02)8:1<93::AID-PIP303>3.0.CO;2-S. 
29. ^ Triple-Junction Terrestrial Concentrator Solar Cells
30. ^ Spire pushes solar cell record to 42.3%. Optics.org. Retrieved on 2011-01-19.
31. ^ [1]^{[dead link]}
32. ^ G24i
33. ^ Konarka Power Plastic reaches 8.3% efficiency. pv-tech.org. Retrieved on 2011-05-07.
34. ^ Mayer, A et al. (2007). "Polymer-based solar cells". Materials Today 10 (11): 28. doi:10.1016/S1369-7021(07)70276-6. 
35. ^ Collins, R (2003). "Evolution of microstructure and phase in amorphous, protocrystalline, and microcrystalline silicon studied by real time spectroscopic ellipsometry". Solar Energy Materials and Solar Cells 78 (1-4): 143. doi:10.1016/S0927-0248(02)00436-1. 
36. ^ J. M. Pearce, N. Podraza, R. W. Collins, M.M. Al-Jassim, K.M. Jones, J. Deng, and C. R. Wronski (2007). "Optimization of Open-Circuit Voltage in Amorphous Silicon Solar Cells with Mixed Phase (Amorphous + Nanocrystalline) p-Type Contacts of Low Nanocrystalline Content". Journal of Applied Physics 101: 114301. doi:10.1063/1.2714507. http://me.queensu.ca/people/pearce/publications/documents/t14.pdf. 
37. ^ Photovoltaics. Engineering.Com (2007-07-09). Retrieved on 2011-01-19.
38. ^ "ANWELL produces its first solar panel". NextInsight. 2009-09-01. http://nextinsight.com.sg/index.php/story-archive-mainmenu-60/36-2009/1480-anwell-produces-its-first-solar-panel. 
39. ^ Widenborg, Per I.; Aberle, Armin G. (2007). "Polycrystalline Silicon Thin-Film Solar Cells on AIT-Textured Glass Superstrates". Advances in OptoElectronics 2007: 1. doi:10.1155/2007/24584. http://downloads.hindawi.com/journals/aoe/2007/024584.pdf. 
40. ^ Terry, Mason L.; Straub, Axel; Inns, Daniel; Song, Dengyuan; Aberle, Armin G. (2005). "Large open-circuit voltage improvement by rapid thermal annealing of evaporated solid-phase-crystallized thin-film silicon solar cells on glass". Applied Physics Letters 86 (17): 172108. doi:10.1063/1.1921352. 
41. ^ Eco-Economy Indicators – Solar Power | EPI. Earth-policy.org. Retrieved on 2011-01-19.
42. ^ March 2011 issue of Photon International
43. ^ "First Solar’s Gift to China: How to Build a Solar Farm". GreentechMedia. 2009-09-10. http://www.greentechmedia.com/articles/read/first-solars-gift-to-china-how-to-build-a-solar-farm/. 
44. ^ EERE News: EERE Network News. Apps1.eere.energy.gov. Retrieved on 2011-01-19.
45. ^ "Solar Firm Aided by Federal Loans Shuts Doors". The New York Times. http://www.nytimes.com/2011/09/01/business/energy-environment/solyndra-solar-firm-aided-by-federal-loans-shuts-doors.html. Retrieved September 2, 2011. 
46. ^ Cheyney, Tom (2010). "Report: Intel spinoff SpectraWatt to lay off workers, shut down solar cell operations". PV-Tech. http://www.pv-tech.org/news/report_intel_spinoff_spectrawatt_to_lay_off_workers_shut_down_operations. Retrieved February 15, 2011. 
47. ^ "Intel solar spinoff SpectraWatt files for bankruptcy". http://news.cnet.com/8301-11128_3-20096841-54/intel-solar-spinoff-spectrawatt-files-for-bankruptcy/. Retrieved September 2, 2011. 

External links

• Photovoltaics CDROM online
• Solar cell manufacturing techniques
• Renewable Energy: Solar at the Open Directory Project
• Solar Energy Laboratory at University of Southampton
• NASA's Photovoltaic Info
• Solar Cell Efficiency Tables (version 36) 2010
• Short educational video on Solar Cells and how they work from the Vega Science Trust
• "Electric Energy From Sun Produced by Light Cell" Popular Mechanics, June 1931 article on various 1930s research on solar cells