Curing (chemistry)

Curing is a term in polymer chemistry and process engineering that refers to the toughening or hardening of a polymer material by cross-linking of polymer chains, brought about by chemical additives, ultraviolet radiation, electron beam or heat. In rubber, the curing process is also called vulcanization.

Resin curing

Despite the wide variety of thermoset resin formulations (epoxy, vinylester, polyester, etc.), their cure behavior is qualitatively identical. The resin viscosity drops initially upon the application of heat, passes through a region of maximum flow and begins to increase as the chemical reactions increase the average length and the degree of cross-linking between the constituent oligomers. This process continues until a continuous 3-dimensional network of oligomer chains is created – this stage is termed gelation. In terms of processability of the resin this marks an important watershed: before gelation the system is relatively mobile, after it the mobility is very limited, the micro-structure of the resin and the composite material is fixed and severe diffusion limitations to further cure are created. Thus in order to achieve vitrification in the resin, it is usually necessary to increase the process temperature after gelation. Cure monitoring methods give a significant insight to the chemical process and define process actions towards achieving specific quality indices of the cured resin systems.

See also

• Concrete curing
• Curing time

References

• Osswald, Tim A.; Menges, Georg (2003). Materials science of polymers for engineers. Hanser Verlag. pp. 334–335. ISBN 9781569903483. http://books.google.de/books?id=84b_MoTo4noC&pg=PA334. 
• Glöckner, Patrick (2009). Radiation Curing. Vincentz Network. pp. 11–16. ISBN 9783866309074. http://books.google.de/books?id=9UyroxckHA4C&pg=PA11.