2024 aluminium alloy

2024 aluminium alloy

Aluminium alloy 2024 is an aluminium alloy, with copper and magnesium as the alloying elements. It is used in applications requiring high strength to weight ratio, as well as good fatigue resistance. It is not weldable, and has average machinability. Due to poor corrosion resistance, it is often clad with aluminium or Al-1Zn for protection, although this may reduce the fatigue strength.

Basic properties

Aluminum alloy 2024 has a density of 2.73 g/cm³ (0.098 lb/in³).

Mechanical properties

The mechanical properties of 2024 depend greatly on the temper of the material. [http://www.alcoa.com/mill_products/catalog/pdf/alloy2024techsheet.pdf Alcoa 2024 data sheet] (pdf), accessed October 13, 2006]

2024-O

2024-O temper aluminium has no heat treating. It has a maximum tensile strength of 30,000-32,000 psi (207-220 MPa), and maximum yield strength of no more than 14,000 psi (96 MPa). The material has elongation (stretch before ultimate failure) of 10-12%.

2024-T3

T3 temper 2024 sheet has an ultimate tensile strength of 58,000-62,000 psi (400-427 MPa) and yield strength of at least 39,000-40,000 psi (269-276 MPa). It has elongation of 10-15%.

2024-T351

T351 temper 2024 plate has an ultimate tensile strength of 68 ksi (470 MPa) and yield strength of 41 kpsi (280 MPa). It has elongation of 19%.

Uses

Due to its high strength and fatigue resistance, 2024 is widely used in aircraft structures, especially wing and fuselage structures under tension. [http://www.aircraftspruce.com/catalog/mepages/aluminfo.php Aluminum Information at aircraftspruce.com] , accessed October 13, 2006] Fundamentals of Flight, Shevell, Richard S., 1989, Englewood Cliffs, Prentice Hall, ISBN 0-13-339060-8, Ch 18, pp 373-386.]

See also

* Aluminum alloy

References

External links

* [http://www.amsmetal.com.sg/products-aluminum.html Aluminum 2024 Trading]


Wikimedia Foundation. 2010.

Игры ⚽ Нужно сделать НИР?

Look at other dictionaries:

  • Aluminium alloy — Aluminium alloys are alloys of aluminium, often with copper, zinc, manganese, silicon, or magnesium. They are much lighter and more corrosion resistant than plain carbon steel, but not quite as corrosion resistant as pure aluminium. Bare… …   Wikipedia

  • Aluminium recycling — is the process by which scrap aluminium can be reused in products after its initial production. The process involves simply re melting the metal, which is far less expensive and energy intensive than creating new aluminium through the… …   Wikipedia

  • Laser peening — is the process of hardening or peening metal using a powerful laser. Laser peening can impart a layer of residual compressive stress on a surface that is four times deeper than that attainable from conventional shot peening treatments. [cite web… …   Wikipedia

  • Manganese — Not to be confused with Magnesium. This article is about the chemical element. For the ghost town, see Manganese, Minnesota. For the steamship, see SS Manganese. chromium ← manganese → iron ↑ Mn ↓ Tc …   Wikipedia

  • Duralumin — Fire damaged Duralumin cross brace from the frame of the Zeppelin airship Hindenburg (DLZ129) salvaged from the crash site at Lakehurst Naval Air Station, NJ, on May 6, 1937 Duralumin (also called duraluminum, duraluminium or dural) is the trade… …   Wikipedia

  • Rivet — A rivet is a mechanical fastener. Before it is installed it consists of a smooth cylindrical shaft with a head on one end. The end opposite the head is called the buck tail. On installation the rivet is placed in a pre drilled hole. Then the tail …   Wikipedia

  • Cessna 152 — Role Multipurpose civil aircraft Manufacturer Cessna Introduction …   Wikipedia

  • aluminum processing — Introduction       preparation of the ore for use in various products.       Aluminum, or aluminium (Al), is a silvery white metal with a melting point of 660° C (1,220° F) and a density of 2.7 grams per cubic centimetre. The most abundant… …   Universalium

  • Désignation des métaux et alliages — En métallurgie, la désignation des métaux et alliages est la désignation normalisée des matériaux métalliques, à indiquer par exemple sur les dessins de pièces. Sommaire 1 Symboles métallurgiques 2 Aluminium et alliages d aluminium …   Wikipédia en Français

  • Designation des metaux et alliages — Désignation des métaux et alliages En métallurgie, la désignation des métaux et alliages est la désignation normalisée des matériaux métalliques, à indiquer par exemple sur les dessins de pièces. Sommaire 1 Aluminium et alliages d aluminium 1.1… …   Wikipédia en Français

Share the article and excerpts

Direct link
… Do a right-click on the link above
and select “Copy Link”