Hypereutectic piston

Hypereutectic piston

“Hypereutectic” means over eutectic. The word eutectic refers to a condition in chemistry when two elements can be alloyed together on a molecular level, but only up to a specific percentage, at which point any additional secondary element will retain a distinct separate form.

Although internal combustion engine pistons commonly contain trace amounts (less than 2% each) of copper, manganese, and nickel, the major element in automotive pistons is aluminium due to its light weight, low cost, and acceptable strength. The alloying element of concern in automotive pistons is silicon. Gold and silver have no eutectic point, which means they can be alloyed together in any ratio, however, when silicon is added to aluminium they only blend together evenly on a molecular level up to approximately a 12% silicon content. For the purposes of this discussion, silicon in this context can be thought of as “powdered sand”. Any silicon that is added to aluminium above a 12% content will retain a distinct granular form instead of melting. At a blend of 25% silicon there is a significant reduction of strength in the piston alloy so stock hypereutectic pistons commonly use a level of silicon between 16% and 19%. Special moulds, casting, and cooling techniques are required to obtain uniformly dispersed silicon particles throughout the piston material.

The reason for their development

Most automotive engines use aluminium pistons that move in a steel cylinder. The average temperature of a piston crown in a gasoline engine during normal operation is typically about 300C (600 degrees Fahrenheit) and the coolant that runs through the engine block is usually regulated at approximately 90C (190 degrees F). Aluminium expands more than steel at this temperature range so for the piston to fit the cylinder properly when at a normal operating temperature, the piston must have a loose fit when cold. In the 1970’s increasing concern over exhaust pollution caused the U.S. government to form the Environmental Protection Agency (EPA) which began passing legislation that forced automobile manufacturers to make changes that allowed their engines to run cleaner.By the late 1980’s automobile exhaust pollution had been noticeably improved but increasingly stringent regulations forced car manufacturers to adopt the use of electronically controlled fuel injection and hypereutectic pistons. It was discovered that when an engine is cold during start-up, a small amount of excess fuel became trapped between the piston rings. As the engine warms up, the piston expands and expels this small amount of fuel which adversely affected the amount of unburnt hydrocarbons in the exhaust.

By adding silicon to the pistons' alloy, the amount the piston expanded could be dramatically reduced. This allowed engineers to specify a much tighter cold-fit between the piston and the cylinder liner. Silicon itself expands less than aluminium but it also acts as an insulator to prevent the aluminium from absorbing as much of the operational heat as it otherwise would.Another beneficial effect of adding silicon is that the piston becomes harder and is less susceptible to scuffing which can occur when a soft aluminium piston is cold-revved in a relatively dry cylinder on start-up.

The biggest drawback of adding silicon to pistons is that the piston becomes more brittle as the ratio of silicon is added. This makes the piston more susceptible to cracking if the engine experiences pre-ignition or detonation.

Performance replacement alloys

When an auto enthusiast wants to increase the power of their engine they often add some type of forced induction. By compressing more air and fuel into each intake cycle, the power of the engine can be dramatically increased. This also increases the heat and pressure in the cylinder. The normal temperature of gasoline engine exhaust is approximately 650C (1200F). This is also approximately the melting point of most aluminium alloys and it is only the constant influx of ambient air that prevents the piston from deforming and failing. Forced induction increases the operating temperatures while “under boost” and if the excess heat is added faster than engine can shed it, the elevated cylinder temperatures will cause the air and fuel mix to auto-ignite on the compression stroke before the spark event. This is one type of engine knocking that causes a sudden shockwave and pressure spike, which can result in an immediate and catastrophic failure of the piston and connecting rod.

The “4032” performance piston alloy has an approximate silicon content of 11%. This means that it expands from heat less than a piston with no silicon, but since its eutectic level of silicon is fully alloyed on a molecular level, this alloy is less brittle and more flexible than a stock hypereutectic “smog” piston. These pistons can survive mild detonation with less damage than stock pistons.

The “2618” performance piston alloy has less than 2% silicon and could be described as hypo (under) eutectic. This alloy is capable of experiencing the most detonation and abuse while suffering the least amount of damage. Pistons made of this alloy are also typically made thicker and heavier because of their most common applications. Because of the higher than normal temperatures these pistons experience in their usual application and also the low-silicon content allowing the maximum possible aluminium heat-expansion, these pistons have their cylinders bored to a very loose cold-fit. This leads to a condition known as “piston slap” which is when the piston rocks in the cylinder and it causes an audible tapping noise that continues until the engine has warmed to operational temperatures. These engines should not be revved when cold, or excessive scuffing can occur.

Forged versus Cast

When a piston is cast the alloy is heated until liquid, then poured into a mould to create the basic shape. After the alloy cools and solidifies it is removed from the mould and the rough casting is machined to its final shape. For applications which require stronger pistons, a forging process is used.

In the forging process the rough casting is placed in a die set while it is still hot and semi-solid. A hydraulic press is used to place the rough slug under tremendous pressure. This removes any possible porosity and also pushes the alloy grains together tighter than can be achieved by simple casting alone. The result is a much stronger material. Hypereutectic pistons can be forged but typically are only cast because the extra expense of forging is not justified when cast pistons are considered strong enough for stock applications.

Aftermarket performance pistons made from the most common 4032 and 2618 alloys are typically forged.


Wikimedia Foundation. 2010.

Игры ⚽ Нужна курсовая?

Look at other dictionaries:

  • Internal combustion engine — The internal combustion engine is an engine in which the combustion of a fuel (normally a fossil fuel) occurs with an oxidizer (usually air) in a combustion chamber. In an internal combustion engine, the expansion of the high temperature and high …   Wikipedia

  • Stroke ratio — In a reciprocating piston engine, the stroke ratio, defined by either bore/stroke ratio or stroke/bore ratio, is a term which is used to describe the ratio between the diameter of the cylinder bore and the length of the piston stroke within its… …   Wikipedia

  • Carburetor — Bendix Technico (Stromberg) 1 barrel downdraft carburetor model BXUV 3, with nomenclature A carburetor (American spelling), carburettor, or carburetter (Commonwealth spelling) is a device that blends air and fuel for an internal combustion engine …   Wikipedia

  • Ignition system — For other uses, see Ignition system (disambiguation). An ignition system is a system for igniting a fuel air mixture. Ignition systems are well known in the field of internal combustion engines such as those used in petrol (gasoline) engines used …   Wikipedia

  • Bore (engine) — Bore is the diameter measurement of the cylinders in a piston engine. Engine displacement is calculated by: The term bore can also be applied to the bore of a locomotive cylinder. See also Stroke (engine) Compression ratio Cylinder head porting… …   Wikipedia

  • Oil pump (internal combustion engine) — This article is about a part in an internal combustion engine. For other uses, see Oil pump. Oil circulation system …   Wikipedia

  • Naturally aspirated engine — A naturally aspirated engine is one common type of reciprocating piston internal combustion engine that depends solely on atmospheric pressure to counter the partial vacuum in the induction tract to draw in combustion air. This is in contrast to… …   Wikipedia

  • Radiator (engine cooling) — For other uses, see Radiator (disambiguation). A typical engine coolant radiator used in an automobile Radiators are used for cooling internal combustion engines, mainly in automobiles but also in piston engined aircraft, railway locomotives,… …   Wikipedia

  • Fuel pump — should not be confused with fuel dispenser, a device that dispenses fuel into an automobile. A high pressure fuel pump on a Yanmar 2GM20 marine diesel engine. A fuel pump is a frequently (but not always) essential component on a car or other… …   Wikipedia

  • Dry sump — A dry sump is a lubricating motor oil management method for four stroke and large two stroke piston internal combustion engines that uses external pumps and a secondary external reservoir for oil, as compared to a conventional wet sump system.… …   Wikipedia

Share the article and excerpts

Direct link
Do a right-click on the link above
and select “Copy Link”