Thin-film deposition

Thin-film deposition

Thin-film deposition is any technique for depositing a thin film of material onto a substrate or onto previously deposited layers. "Thin" is a relative term, but most deposition techniques allow layer thickness to be controlled within a few tens of nanometers, and some (molecular beam epitaxy) allow single layers of atoms to be deposited at a time.

It is useful in the manufacture of optics (for reflective or anti-reflective coatings, for instance), electronics (layers of insulators, semiconductors, and conductors form integrated circuits), packaging (i.e., aluminum-coated PET film), and in contemporary art (see the work of Larry Bell). Similar processes are sometimes used where thickness is not important: for instance, the purification of copper by electroplating, and the deposition of silicon and enriched uranium by a CVD-like process after gas-phase processing.

Deposition techniques fall into two broad categories, depending on whether the process is primarily chemical or physical.

Chemical deposition

Here, a fluid undergoes a chemical change at a solid surface, leaving a solid layer. An everyday example is the formation of soot on a cool object when it is placed inside a flame. Since the fluid surrounds the solid object, deposition happens on every surface, with little regard to direction; thin films from chemical deposition techniques tend to be "conformal", rather than "directional".

Chemical deposition is further categorized by the phase of the precursor:

* Plating relies on liquid precursors, often a solution of water with a salt of the metal to be deposited. Some plating processes are driven entirely by reagents in the solution (usually for noble metals), but by far the most commercially important process is electroplating. It was not commonly used in semiconductor processing for many years, but has seen a resurgence with more widespread use of Chemical-mechanical polishing techniques.

*Chemical Solution Deposition (CSD) uses a liquid precursor, usually a solution of organometallic powders dissolved in an organic solvent. This is a relatively inexpensive, simple thin film process that is able to produce stoichiometrically accurate crystalline phases.

* Chemical vapor deposition (CVD) generally uses a gas-phase precursor, often a halide or hydride of the element to be deposited. In the case of MOCVD, an organometallic gas is used. Commercial techniques often use very low pressures of precursor gas.
** Plasma enhanced CVD uses an ionized vapor, or plasma, as a precursor. Unlike the soot example above, commercial PECVD relies on electromagnetic means (electric current, microwave excitation), rather than a chemical reaction, to produce a plasma.

Physical deposition

Physical deposition uses mechanical or thermodynamic means to produce a thin film of solid. An everyday example is the formation of frost. Since most engineering materials are held together by relatively high energies, and chemical reactions are not used to store these energies, commercial physical deposition systems tend to require a low-pressure vapor environment to function properly; most can be classified as Physical vapor deposition or PVD.

The material to be deposited is placed in an energetic, entropic environment, so that particles of material escape its surface. Facing this source is a cooler surface which draws energy from these particles as they arrive, allowing them to form a solid layer. The whole system is kept in a vacuum deposition chamber, to allow the particles to travel as freely as possible. Since particles tend to follow a straight path, films deposited by physical means are commonly "directional", rather than "conformal".

Examples of physical deposition include:

* A thermal evaporator uses an electric resistance heater to melt the material and raise its vapor pressure to a useful range. This is done in a high vacuum, both to allow the vapor to reach the substrate without reacting with or scattering against other gas-phase atoms in the chamber, and reduce the incorporation of impurities from the residual gas in the vacuum chamber. Obviously, only materials with a much higher vapor pressure than the heating element can be deposited without contamination of the film. Molecular beam epitaxy is a particular sophisticated form of thermal evaporation.
** An electron beam evaporator fires a high-energy beam from an electron gun to boil a small spot of material; since the heating is not uniform, lower vapor pressure materials can be deposited. The beam is usually bent through an angle of 270° in order to ensure that the gun filament is not directly exposed to the evaporant flux. Typical deposition rates for electron beam evaporation range from 1 to 10 nanometers per second.

*Sputtering relies on a plasma (usually a noble gas, such as Argon) to knock material from a "target" a few atoms at a time. The target can be kept at a relatively low temperature, since the process is not one of evaporation, making this one of the most flexible deposition techniques. It is especially useful for compounds or mixtures, where different components would otherwise tend to evaporate at different rates. Note, Sputtering's step coverage is more or less conformal.

*Pulsed laser deposition systems work by an ablation process. Pulses of focused laser light vaporize the surface of the target material and convert it to plasma; this plasma usually reverts to a gas before it reaches the substrate.

*Cathodic Arc Deposition or Arc-PVD which is a kind of ion beam deposition where an electrical arc is created that literally blasts ions from the cathode. The arc has an extremely high power density resulting in a high level of ionization (30-100%), multiply charged ions, neutral particles, clusters and macro-particles (droplets). If a reactive gas is introduced during the evaporation process, dissociation, ionization and excitation can occur during interaction with the ion flux and a compound film will be deposited.

Other deposition processes

Some methods fall outside these two categories, relying on a mixture of chemical and physical means:

* In reactive sputtering, a small amount of some non-noble gas such as oxygen or nitrogen is mixed with the plasma-forming gas. After the material is sputtered from the target, it reacts with this gas, so that the deposited film is a different material, i.e. an oxide or nitride of the target material.

* In Molecular beam epitaxy (MBE), slow streams of an element can be directed at the substrate, so that material deposits one atomic layer at a time. Compounds such as gallium arsenide are usually deposited by repeatedly applying a layer of one element (i.e., Ga), then a layer of the other (i.e., As), so that the process is chemical, as well as physical. The beam of material can be generated by either physical means (that is, by a furnace) or by a chemical reaction (chemical beam epitaxy).

* In Topotaxy, a specialized technique similar to epitaxy, thin film crystal growth occurs in three dimensions due to the crystal structure similarities (either heterotopotaxy or homotopotaxy) between the substrate crystal and the growing thin film material.

ee also

* Materials science
* Photolithography
* CVD, MBE, and Sputtering
* List of coating techniques
* Thin-film thickness monitor
* VINF Virtual Institute of Nanofilms

External links

* [ ORNL] (Oak Ridge National Laboratory)

Wikimedia Foundation. 2010.

Игры ⚽ Нужен реферат?

Look at other dictionaries:

  • thin-film deposition — plonųjų sluoksnių nusodinimas statusas T sritis radioelektronika atitikmenys: angl. thin film deposition vok. Dünnschichtabscheidung, f rus. осаждение тонких плёнок, n pranc. déposition de film mince, f; déposition des couches minces, f …   Radioelektronikos terminų žodynas

  • Thin film — A thin film is a layer of material ranging from fractions of a nanometer (monolayer) to several micrometers in thickness. Electronic semiconductor devices and optical coatings are the main applications benefiting from thin film construction. A… …   Wikipedia

  • Thin-film thickness monitor — Thin film thickness monitors, deposition rate controllers, and so on, are a family of instruments used in high and ultra high vacuum systems. They can measure the thickness of a thin film, not only after it has been made, but while it is still… …   Wikipedia

  • thin-film — thinˈ film adjective (electronics) Made by chemical or physical vapour deposition or electrolysis, typically no more than a few micrometres thick • • • Main Entry: ↑thin * * * adj. (of a process or device) using or involving a very thin solid or… …   Useful english dictionary

  • Thin film solar cell — Cross section of thin film polycrystalline solar cell. A thin film solar cell (TFSC), also called a thin film photovoltaic cell (TFPV), is a solar cell that is made by depositing one or more thin layers (thin film) of photovoltaic material on a… …   Wikipedia

  • Thin-film optics — Dichroic filters are created using thin film optics. A pattern …   Wikipedia

  • Thin-film transistor — A thin film transistor (TFT) is a special kind of field effect transistor made by depositing thin films of a semiconductor active layer as well as the dielectric layer and metallic contacts over a supporting substrate. A common substrate is glass …   Wikipedia

  • thin-film — /ˈθɪn fɪlm/ (say thin film) adjective of or relating to the deposition of metals over insulating substrates, as for the making of magnetic films for certain computer memories …  

  • Deposition — or Depose may refer to: Deposition (law), taking testimony outside of court Deposition (chemistry), molecules settling out of a solution Thin film deposition, any technique for depositing a thin film of material onto a substrate or onto… …   Wikipedia

  • Thin — may refer to:* Thin client, computer in client server architecture networks * Thin film, material layer of about 1 µm thickness * Thin film memory, high speed variation of core memory developed by Sperry Rand in a government funded research… …   Wikipedia

Share the article and excerpts

Direct link
Do a right-click on the link above
and select “Copy Link”