Coke strength after reaction

Coke strength after reaction

Coke Strength after Reaction (CSR) refers to coke "hot" strength, generally a quality reference in a simulated reaction condition in an industrial blast furnace. The test is based on a procedure developed by Nippon Steel Corp in the 1970s as an attempt to get an indication of coke performance and is used widely throughout the world since then. It is one of the major considerations when blending coking coal for export sale.[1]

Test procedure

In the test, a 200 g sample of –21 mm to +19 mm particle range coke is heated at 1100 °C under 1 atmosphere pressure of carbon dioxide for 2 hours. The coke is preheated and cooled under nitrogen and the weight loss during reaction is measured. The percentage weight loss is known as the reactivity (CRI). The reacted coke is placed in an I-type drum (no lifters) and subjected to 600 revolutions in 30 minutes. The percent of carbon material removed from the drum that is +10 mm is known as the coke strength after reaction (CSR). [2]

References

  1. ^ http://www.chinacoke.com/reactivity.cfm
  2. ^ Reifensteinin (2003) ACARP Report C12004 Coke Reactivity Test: Critical Parameters



Wikimedia Foundation. 2010.

Игры ⚽ Нужно решить контрольную?

Look at other dictionaries:

  • Coke (fuel) — This article is about fuel coke derived from coal. For fuel coke derived from petroleum, see Petroleum coke. For other uses, see Coke. Raw coke Coke is the solid carbonaceous material derived from destructive distillation of low ash, low sulfur… …   Wikipedia

  • Edward Coke — This article is about the seventeenth century jurist. For other uses, see Edward Coke (disambiguation). Sir Edward Coke …   Wikipedia

  • ГОСТ Р 54250-2010: Кокс. Определение реакционной способности кокса (CRI) и прочности кокса после реакции (CSR) — Терминология ГОСТ Р 54250 2010: Кокс. Определение реакционной способности кокса (CRI) и прочности кокса после реакции (CSR) оригинал документа: 3.1 показатель истирания (abrasion value): Потеря коксом устойчивости к истиранию после реакции с… …   Словарь-справочник терминов нормативно-технической документации

  • порция — 3.11 порция: Масса или объем блюда, предназначенные для однократного приема одним потребителем. Источник …   Словарь-справочник терминов нормативно-технической документации

  • порция (test portion) — 3.3 порция (test portion): Представительная часть пробы, непосредственно подвергаемая испытанию. 3.4 прочность кокса после реакции с двуокисью углерода, CSR (coke strength after reaction CSR): Прочность кокса после реакции с двуокисью углерода… …   Словарь-справочник терминов нормативно-технической документации

  • metallurgy — metallurgic, metallurgical, adj. metallurgically, adv. metallurgist /met l err jist/ or, esp. Brit., /meuh tal euhr jist/, n. /met l err jee/ or, esp. Brit., /meuh tal euhr jee/, n. 1. the technique or science of working or heating metals so as… …   Universalium

  • steel — steellike, adj. /steel/, n. 1. any of various modified forms of iron, artificially produced, having a carbon content less than that of pig iron and more than that of wrought iron, and having qualities of hardness, elasticity, and strength varying …   Universalium

  • MythBusters (2006 season) — Country of origin Australia United States No. of episodes 28 (includes 2 specials) Broadcast Original channel Discovery Channel …   Wikipedia

  • United Kingdom — a kingdom in NW Europe, consisting of Great Britain and Northern Ireland: formerly comprising Great Britain and Ireland 1801 1922. 58,610,182; 94,242 sq. mi. (244,100 sq. km). Cap.: London. Abbr.: U.K. Official name, United Kingdom of Great… …   Universalium

  • chemical industry — Introduction       complex of processes, operations, and organizations engaged in the manufacture of chemicals and their derivatives.       Although the chemical industry may be described simply as the industry that uses chemistry and… …   Universalium

Share the article and excerpts

Direct link
Do a right-click on the link above
and select “Copy Link”