Crevice corrosion

Crevice corrosion

Crevice corrosion refers to corrosion occurring in confined spaces to which the access of the working fluid from the environment is limited. These spaces are generally called crevices. Examples of crevices are gaps and contact areas between parts, under gaskets or seals, inside cracks and seams, spaces filled with deposits and under sludge piles.

Crevice corrosion of type 316 stainless steel

This photo shows that corrosion occurred in the crevice between the tube and tube sheet (both made of type 316 stainless steel) of a heat exchanger in a sea water desalination plant.[1]

Contents

Mechanism

The corrosion resistance of a stainless steel is dependent on the presence of an ultra-thin protective oxide film (passive film) on its surface, but it is possible under certain conditions for this oxide film to break down, for example in halide solutions or reducing acids. Areas where the oxide film can break down can also sometimes be the result of the way components are designed, for example under gaskets, in sharp re-entrant corners or associated with incomplete weld penetration or overlapping surfaces. These can all form crevices which can promote corrosion. To function as a corrosion site, a crevice has to be of sufficient width to permit entry of the corrodent, but narrow enough to ensure that the corrodent remains stagnant. Accordingly crevice corrosion usually occurs in gaps a few micrometres wide, and is not found in grooves or slots in which circulation of the corrodent is possible. This problem can often be overcome by paying attention to the design of the component, in particular to avoiding formation of crevices or at least keeping them as open as possible. Crevice corrosion is a very similar mechanism to pitting corrosion; alloys resistant to one are generally resistant to both. Crevice corrosion can be viewed as a less severe form of localized corrosion when compared with pitting. The depth of penetration and the rate of propagation in pitting corrosion are significanatly greater than in crevice corrosion.

Crevices can develop a local chemistry which is very different from that of the bulk fluid. For example, in boilers, concentration of non-volatile impurities may occur in crevices near heat-transfer surfaces because of the continuous water vaporization. "Concentration factors" of many millions are not uncommon for common water impurities like sodium, sulfate or chloride. The concentration process is often referred to as "hideout" (HO), whereas the opposite process, whereby the concentrations tend to even out (e.g., during shutdown) is called "hideout return" (HOR). In a neutral pH solution, the pH inside the crevice can drop to 2, a highly acidic condition that accelerates the corrosion of most metals and alloys.

For a given crevice type, two factors are important in the initiation of crevice corrosion: the chemical composition of the electrolyte in the crevice and the potential drop into the crevice. Researchers had previously claimed that either one or the other of the two factors was responsible for initiating crevice corrosion, but recently it has been shown that it is a combination of the two that causes active crevice corrosion [2]. Both the potential drop and the change in composition of the crevice electrolyte are caused by deoxygenation of the crevice and a separation of electroactive areas, with net anodic reactions occurring within the crevice and net cathodic reactions occurring exterior to the crevice (on the bold surface). The ratio of the surface areas between the cathodic and anodic region is significant.

Some of the phenomena occurring within the crevice may be somewhat reminiscent of galvanic corrosion:

galvanic corrosion
two connected metals + single environment
crevice corrosion
one metal part + two connected environments

The mechanism of crevice corrosion can be (but is not always) similar to that of pitting corrosion. However, there are sufficient differences to warrant a separate treatment. For example, in crevice corrosion, one has to consider the geometry of the crevice and the nature of the concentration process leading to the development of the differential local chemistry. The extreme and often unexpected local chemistry conditions inside the crevice need to be considered. Galvanic effects can play a role in crevice degradation.

Mode of attack

Depending on the environment developed in the crevice and the nature of the metal, the crevice corrosion can take a form of:

  • pitting (i.e., formation of pits),
  • filiform corrosion (this type of crevice corrosion that may occur on an aluminium surface underneath an organic coating),
  • intergrannular attack, or
  • stress corrosion cracking.

Stress corrosion cracking

The Silver Bridge upon completion in 1928
The collapsed Silver Bridge, as seen from the Ohio side

A common form of crevice failure occurs due to stress corrosion cracking, where a crack or cracks develop from the base of the crevice where the stress concentration is greatest. This was the root cause of the fall of the Silver Bridge in 1967 in West Virginia, where a single critical crack only about 3 mm long suddenly grew and fractured a tie bar joint. The rest of the bridge fell in less than a minute. The eyebars in the Silver Bridge were not redundant, as links were composed of only two bars each, of high strength steel (more than twice as strong as common mild steel), rather than a thick stack of thinner bars of modest material strength "combed" together as is usual for redundancy. With only two bars, the failure of one could impose excessive loading on the second, causing total failure—unlikely if more bars are used. While a low-redundancy chain can be engineered to the design requirements, the safety is completely dependent upon correct, high quality manufacturing and assembly.

Significance

The susceptibility to crevice corrosion varies widely from one material-environment system to another. In general, crevice corrosion is of greatest concern for materials which are normally passive metals, like stainless steel or aluminum. Crevice corrosion tends to be of greatest significance to components built of highly corrosion-resistant superalloys and operating with the purest-available water chemistry. For example, steam generators in nuclear power plants degrade largely by crevice corrosion.

Crevice corrosion is extremely dangerous because it is localized and can lead to component failure while the overall material loss is minimal. The initiation and progress of crevice corrosion can be difficult to detect.

References

  1. ^ Crevice Corrosion
  2. ^ Kennell, G.F., K.L. Heppner, R.W. Evitts. (2008) A Critical Crevice Solution and iR Drop Crevice Corrosion Model. Corrosion Science 50: 1716.

External links


Wikimedia Foundation. 2010.

Игры ⚽ Нужна курсовая?

Look at other dictionaries:

  • Crevice corrosion — Crevice corrosion. См. Щелевая коррозия. (Источник: «Металлы и сплавы. Справочник.» Под редакцией Ю.П. Солнцева; НПО Профессионал , НПО Мир и семья ; Санкт Петербург, 2003 г.) …   Словарь металлургических терминов

  • crevice corrosion — plyšinė korozija statusas T sritis chemija apibrėžtis Metalų korozija siaurose angose ar tarpuose. atitikmenys: angl. crevice corrosion rus. щелевая коррозия …   Chemijos terminų aiškinamasis žodynas

  • Corrosion — v · d · e Materials failure modes Buckling · …   Wikipedia

  • Crevice — A crevice usually refers to a fracture or fissure in rock (compare to a crevasse, which is in ice). Crevice may also refer to: Crevice corrosion, occurs in spaces to which the access of corrosion resistant fluid is limited Crevice kelpfish… …   Wikipedia

  • Pitting corrosion — Pitting corrosion, or pitting, is a form of extremely localized corrosion that leads to the creation of small holes in the metal. The driving power for pitting corrosion is the depassivation of a small area, which becomes anodic while an unknown… …   Wikipedia

  • localized corrosion — Rusting occurring at one part of a metal surface at a much higher rate than over the rest of the surface, e.g., pitting corrosion, crevice corrosion. The opposite is uniform corrosion …   Dictionary of automotive terms

  • Stress corrosion cracking — (SCC) is the unexpected sudden failure of normally ductile metals or tough thermoplastics subjected to a tensile stress in a corrosive environment, especially at elevated temperature (in the case of metals). SCC is highly chemically specific in… …   Wikipedia

  • Щелевая коррозия — Crevice corrosion Щелевая коррозия. Местная коррозия металлической поверхности в местах перехода толщин, сопряжения поверхностей, зазорах между металлом и другими материалами. (Источник: «Металлы и сплавы. Справочник.» Под редакцией Ю.П.… …   Словарь металлургических терминов

  • Fouling — This article is about fouling in engineering. For uses of the term foul outside technology, see Foul (disambiguation). Not to be confused with fowling. Heat exchanger in a steam power plant, fouled by macro fouling …   Wikipedia

  • Stainless steel — Iron alloy phases Ferrite (α iron, δ iron) Austenite (γ iron) Pearlite (88% ferrite, 12% cementite) …   Wikipedia

Share the article and excerpts

Direct link
Do a right-click on the link above
and select “Copy Link”