Austempering

Austempering

Austempering is a hardening process that is used on metals to promote better mechanical properties.

These properties include:
* Higher ductility
* Resistance to shock
* Uniform Hardness

The Process

The metal is heated into the austenite region and then immediately quenched in a "salt bath" or heat extraction medium that is between temperatures of 570 - 710 degrees Fahrenheit. The metal is held here until the austenite turns to bainite.

Other heat treatments start the same but quench in a medium that is closer to room temperature causing martensite to form. Martensite is a much more brittle material and since the "salt bath" is heated above this region a new structure results

Advantages

* Less Distortion
* Greater Ductility
* Parts are plater friendly due to the clean surface from the salt quench
* Uniform and consistent Hardness
* Tougher and More Wear Resistant
* Higher Impact and Fatigue Strengths
* Resistance to Hydrogen Embrittlement


Wikimedia Foundation. 2010.

Игры ⚽ Поможем сделать НИР

Look at other dictionaries:

  • Austempering — Saltar a navegación, búsqueda Diagrama de transformación isotérmica El austempering es un tratamiento térmico que se aplica al Acero. Con este tratamiento isotérmico se pretende obtener piezas con una estructura bainítica, que sean duras pero no… …   Wikipedia Español

  • Austempering — Austempering. См. Изотермическая закалка на бейнит. (Источник: «Металлы и сплавы. Справочник.» Под редакцией Ю.П. Солнцева; НПО Профессионал , НПО Мир и семья ; Санкт Петербург, 2003 г.) …   Словарь металлургических терминов

  • austempering — (voz inglesa) ► masculino METALURGIA Proceso de endurecimiento del acero que consiste en templar la pieza pasando de la temperatura austenítica hasta otra intermedia que se mantiene durante un tiempo suficiente; también es llamado temple… …   Enciclopedia Universal

  • austempering — Смотри изотермическая закалка …   Энциклопедический словарь по металлургии

  • austempering — quenching from a temperature above the transformation range to a temperature above the upper limit of martensite formation, and holding at this temperature until the austenite is completely transformed to the desired intermediate structure, for… …   Mechanics glossary

  • austempering — Trattamento termico nel quale l austenite è raffreddata fino ad una temperatura costante (superiore ad Ms), in modo da ottenere una completa trasformazione bainitica. In alcuni acciai, per alcuni livelli di durezze, la bainite presenta una… …   Glossario di Metallurgia

  • austempering — …   Useful english dictionary

  • Изотермическая закалка на бейнит — Austempering Изотермическая закалка на бейнит. Термообработка сталей, при которой сплав нагретый до температуры аустенитизации охлаждают с достаточно высокой скоростью, чтобы избежать образования феррита и перлита, и затем выдерживают при… …   Словарь металлургических терминов

  • изотермическая закалка — [austempering] закалка, включающая аустенитизацию стали, быстрое охлаждение в температурную область относительной устойчивости переохлажденного аустенита и выдержку до полного или частичного превращения аустенита в бейнит (Смотри Бейнит).… …   Энциклопедический словарь по металлургии

  • Carbon steel — Iron alloy phases Ferrite (α iron, δ iron) Austenite (γ iron) Pearlite (88% ferrite, 12% cementite) …   Wikipedia

Share the article and excerpts

Direct link
… Do a right-click on the link above
and select “Copy Link”