Segregation in materials

Segregation in materials

Segregation in Materials refers to the enrichment of a material constituent at a free surface or an internal interface of a material. In a polycrystalline solid, a segregation site can be a dislocation, grain boundary, stacking fault, or an interface with a precipitate or secondary phase within the solid. There are two recognized types of segregation: equilibrium segregation and non-equilibrium segregation.


Equilibrium segregation is associated with the lattice disorder at interfaces, where there are sites of energy different from those within the lattice at which the solute atoms can deposit themselves. The equilibrium segregation is so termed because the solute atoms segregate themselves to the interface or surface in accordance of with the statistics of thermodynamics in order to minimize the overall free energy of the system. This sort of partitioning of solute atoms between the grain boundary and the lattice was predicted by McLean in 1957 [1] .

Non-equilibrium segregation, first theorized by Westbrook in 1964 [2] , occurs as a result of solutes coupling to vacancies which are moving to grain boundary sources or sinks during quenching or application of stress. It can also occur as a result of solute pile-up at a moving interface [3] .

There are two main features of non-equilibrium segregation, by which it is most easily distinguished from equilibrium segregation. In the non-equilibrium effect, the magnitude of the segregation increases with increasing temperature and the alloy can be homogenized without further quenching because its lowest energy state corresponds to a uniform solute distribution. In contrast, the equilibrium segregated state, by definition, is the lowest energy state in a system that exhibits equilibrium segregation, and the extent of the segregation effect decreases with increasing temperature. The details of non-equilibrium segregation are not going to be discussed here, but can be found in the review by Harries and Marwick [4] .

Why is segregation important?

Segregation of a solute to surfaces and grain boundaries in a solid produces a section of material with a discrete composition and its own set of properties that can have important (and often deleterious effects) on the overall properties of the material. These ‘zones’ with an increased concentration of solute can be thought of as the cement between the bricks of a building. The structural integrity of the building depends not only on the material properties of the brick, but also greatly on the properties of the long lines of mortar in between.

Segregation to grain boundaries, for example, can lead to grain boundary fracture as a result of temper brittleness, creep embrittlement, stress relief cracking of weldments, hydrogen embrittlement, environmentally assisted fatigue, grain boundary corrosion, and some kinds of intergranular stress corrosion cracking [5] . Segregation to grain boundaries can also affect their respective migration rates, and so affects sinterability, as well as the grain boundary diffusivity (although sometimes these effects can be used advantageously) [6] .

Segregation to free surfaces also has important consequences involving the purity of metallurgical samples. Because of the favorable segregation of some impurities to the surface of the material, a very small concentration of impurity in the bulk of the sample can lead to a very significant coverage of the impurity on a cleaved surface of the sample. In applications where an ultra-pure surface is needed (for example, in some nanotechnology applications), the segregation of impurities to surfaces requires a much higher purity of bulk material than would be needed if segregation effects didn’t exist. The following figure illustrates this concept with two cases in which the total fraction of impurity atoms is 0.25 (25 impurity atoms in 100 total). In the representation on the left, these impurities are equally distributed throughout the sample, and so the fractional surface coverage of impurity atoms is also approximately 0.25. In the representation to the right, however, the same number of impurity atoms are shown segregated on the surface, so that an observation of the surface composition would yield a much higher impurity fraction (in this case, about 0.69). In fact, in this example, were impurities to completely segregate to the surface, an impurity fraction of just 0.36 could completely cover the surface of the material. In an application where surface interactions are important, this result could be disastrous.

It is important to note that while the intergranular failure problems noted above are sometimes severe, they are rarely the cause of major service failures (in structural steels, for example), as suitable safety margins are included in the designs. Perhaps the greater concern is that with the development of new technologies and materials with new and more extensive mechanical property requirements, and with the increasing impurity contents as a result of the increased recycling of materials, we may see intergranular failure in materials and situations not seen currently. Thus, a greater understanding of all of the mechanisms surrounding segregation might lead to being able to control these effects in the future [6] . Modeling potentials, experimental work, and related theories are still being developed to explain these segregation mechanisms for increasingly complex systems.

Theories of Segregation

Several theories describe the equilibrium segregation activity in materials. The adsorption theories for the solid-solid interface and the solid-vacuum surface are direct analogues of theories well known in the field of gas adsorption on the free surfaces of solids [7] .

Langmuir-McLean theory for surface and grain boundary segregation in binary systems

This is the earliest theory specifically for grain boundaries, in which McLean [1] uses a model of P solute atoms distributed at random amongst N lattice sites and p solute atoms distributed at random amongst n independent grain boundary sites. The total free energy due to the solute atoms is then:

G = pe + PE - kT [ln(n!N!) - ln(n - p)!p!(N - P)!P!]

where E and e are energies of the solute atom in the lattice and in the grain boundary, respectively and the kln term represents the configurational entropy of the arrangement of the solute atoms in the bulk and grain boundary. McLean used basic statistical mechanics to find the fractional monolayer of segregant, X_b, at which the system energy was minimized (at the equilibrium state), differentiating G with respect to p, noting that the sum of p an P is constant. Here the grain boundary analogue of Langmuir adsorption at free surfaces becomes:

frac{X_b}{X_b^0-X_b}=frac{X_c}{1-X_c}exp left ( frac{-Delta,G}{RT} ight )

Here, X_b^0 is the fraction of the grain boundary monolayer available for segregated atoms at saturation, X_b is the actual fraction covered with segregant, X_c is the bulk solute molar fraction, and Delta,G is the free energy of segregation per mole of solute.

Values of Delta,G were estimated by McLean using the elastic strain energy, E_{el}, released by the segregation of solute atoms. The solute atom is represented by an elastic sphere fitted into a spherical hole in an elastic matrix continuum. The elastic energy associated with the solute atom is given by:

E_{el}=frac{24pi,Kappa,mu,_0 r_0 (r_1-r_0)^2}{3Kappa,+4mu,_0}

where Kappa, is the solute bulk modulus, mu,_0, is the matrix shear modulus, and r_0, and r_1, are the atomic radii of the matrix and impurity atoms, respectively. This method gives values correct to within a factor of two (as compared with experimental data for grain boundary segregation), but a greater accuracy is obtained using the method of Seah and Hondros [8] , described in the following section.

Free energy of grain boundary segregation in binary systems

Using truncated BET theory (the gas adsorption theory developed by Brunauer, Deming, Deming, and Teller), Seah and Hondros [8] write the solid-state analogue as:

frac{X_b}{X_b^0-X_b}=frac{X_c}{X_c^0}exp left ( frac{-Delta G'}{RT} ight )

where Delta,G=Delta,G' + Delta,G_{sol}

X_c^0 is the solid solubility, which is known for many elements (and can be found in metallurgical handbooks). Note that in the dilute limit, a slightly soluble substance has X_c^0 = exp left ( frac{Delta,G_{sol{RT} ight ), so the above equation reduces to that found with the Langmuir-McLean theory. Note also that this equation is only valid for X_c le X_c^0. If there is an excess of solute such that a second phase appears, the solute content is limited to X_c^0 and the equation becomes

frac{X_b}{X_b^0-X_b} = exp left ( frac{-Delta,G'}{RT} ight )

This theory for grain boundary segregation, derived from truncated BET theory, provides excellent agreement with experimental data obtained by Auger electron spectroscopy and other techniques [7] .

More complex systems

Other models exist to model more complex binary systems [7] . The above theories operate on the assumption that the segregated atoms are non-interacting. If, in a binary system, adjacent adsorbate atoms are allowed an interaction energy omega,, such that they can attract (when omega, is negative) or repel (when omega, is positive) each other, the solid-state analogue of the Fowler adsorption theory is developed as:

frac {X_b}{X_b^0 - X_b} = frac {X_c}{1-X_c} exp left [ frac{-Delta,G - Z_1omega,frac{X_b}{X_b^0{RT} ight ]

Note that when omega, is zero, this theory reduces to that of Langmuir and McLean. However, as omega, becomes more negative, the segregation shows progressively sharper rises as the temperature falls until eventually the rise in segregation is discontinuous at a certain temperature, as shown in the following figure.

Guttman, in 1975, extended the Fowler theory to allow for interactions between two co-segregating species in multicomponent systems. This modification is vital to explaining the segregation behavior that results in the intergranular failures of engineering materials. More complex theories are detailed in the work by Guttmann [9] and McLean and Guttmann [10] .

The free energy of surface segregation in binary systems

The Langmuir-McLean equation for segregation, when using the regular solution model for a binary system, is valid for surface segregation (although sometimes the equation will be written replacing X_b with X_s) [11] . The free energy of surface segregation is Delta,G_s = Delta,H_s - TDelta,S. The enthalpy is given by

-Delta,H_s = gamma,_0^s - gamma,_1^s - frac{2H_m}{ZX_c(1-X_c)}left [ Z_1 (X_c-X_s) + Z_v left (X_c - frac {1}{2} ight ) ight ] + frac {24pi,Kappa,mu,_0 r_0 (r_1-r_0)^2}{3Kappa,+4mu,_0}

where gamma,_0 and gamma,_1 are matrix surface energies without and with solute, H_1 is their heat of mixing, Z and Z_1 are the coordination numbers in the matrix and at the surface, and Z_v is the coordination number for surface atoms to the layer below. The last term in this equation is the elastic strain energy E_(el), given above, and is governed by the mismatch between the solute and the matrix atoms. For solid metals, the surface energies scale with the melting points. The surface segregation enrichment ratio increases when the solute atom size is larger than the matrix atom size and when the melting point of the solute is lower than that of the matrix [7] .

A chemisorbed gaseous species on the surface can also have an effect on the surface composition of a binary alloy. In the presence of a coverage of a chemisorbed species theta, it is proposed that the Langmuir-McLean model is valid with the free energy of surface segregation given by Delta,G_{chem} [12] , where

Delta,G_{chem} = Delta,G_s + (E_B - E_A)Theta,

E_A and E_B are the chemisorption energies of the gas on solute A and matrix B and Θ is the fractional coverage. At high temperatures, evaporation from the surface can take place, causing a deviation from the McLean equation. At lower temperatures, both grain boundary and surface segregation can be limited by the diffusion of atoms from the bulk to the surface or interface.

Kinetics of Segregation

In some situations where segregation is important, the segregant atoms do not have sufficient time to reach their equilibrium level as defined by the above adsorption theories. The kinetics of segregation become a limiting factor and must be analyzed as well. Most existing models of segregation kinetics follow the McLean approach. In the model for equilibrium monolayer segregation, the solute atoms are assumed to segregate to a grain boundary from two infinite half-crystals or to a surface from one infinite half-crystal. The diffusion in the crystals is described by Fick’s laws. The ratio of the solute concentration in the grain boundary to that in the adjacent atomic layer of the bulk is given by an enrichment ratio, β. Most models assume β to be a constant, but in practice this is only true for dilute systems with low segregation levels. In this dilute limit, if X_b^0 is one monolayer, β is given as β = frac{X_b}{X_c} =frac {expleft (frac{-Delta,G'}{RT} ight )}{X_c^0}.

The kinetics of segregation can be described by the following equation:

frac{X_{b}(t) - X_{b}(0)}{X_{b}(infin,) - X_{b}(0)} = 1 - exp left ( frac {FDt}{eta,^2f^2} ight ) erfc left ( frac {FDt}{eta,^2f^2} ight )^{frac{1}{2

Where F=4 four grain boundaries and 1 for the free surface, X_{b}(t) is the boundary content at time t, D is the solute bulk diffusivity, f is related to the atom sizes of the solute and the matrix, b and a, respectively, by f = a^3b^{-2}. For short times, this equation is approximated by:

frac{X_b(t) - X_b(0)}{X_b(infin,) - X_b(0)} = frac {2}{eta,} frac {b^2}{a^2} sqrt{frac {FDt}{pi,

In practice, β is not a constant but generally falls as segregation proceeds due to saturation. If β starts high and falls rapidly as the segregation saturates, the above equation is valid until the point of saturation [7] .


#D. McLean: Grain Boundaries in Metals, Oxford University Press, London (1957)
#J. H. Westbrook, Metall. Rev. 9, 415-70 (1964)
#J. R. Rellick, C. J. McMahon, Metall. Trans. 5, 2439-50 (1974)
#D. R. Harries, A. D. Marwick, Phil. Trans. R. Soc. A 295, 197-207 (1980)
#M. P. Seah, Journal of Catalysis 57, 450-457 (1979)
#M. P. Seah, J. Phys. F: Metal Phys. 10, 1043-64 (1980)
#D. Briggs, M.P. Seah (Ed.), Practical Surface Analysis by Auger and X-ray Photoelectron Spectroscopy, John Wiley & Sons, (1983)
#M. P. Seah, E. D. Hondros, Proc. Roy. Soc. London A335, 191 (1973)
#M. Guttmann, D. McLean, in Interfacial Segreation (Eds W. C. Johnson and J.M. Blakely), American Society for Metals, Metals Park (1979)
#M. Gutmann, Phil. Trans. Roy. Soc. A295, 169 (1980)
#P. Wynblatt, R.C. Ku in Interfacial Segregation (Eds. W.C. Johnson, J.M. Blakely), American Society for Metals, Metals Park (1979)
#J.R. Rice, J.S. Wang, Mat. Sci. Eng. A107, 23 (1989)

Wikimedia Foundation. 2010.

Игры ⚽ Нужен реферат?

Look at other dictionaries:

  • Racism — Part of a series on …   Wikipedia

  • Grain boundary — A grain boundary is the interface between two grains in a polycrystalline material. Grain boundaries disrupt the motion of dislocations through a material, so reducing crystallite size is a common way to improve strength, as described by the Hall …   Wikipedia

  • earth — /errth/, n. 1. (often cap.) the planet third in order from the sun, having an equatorial diameter of 7926 mi. (12,755 km) and a polar diameter of 7900 mi. (12,714 km), a mean distance from the sun of 92.9 million mi. (149.6 million km), and a… …   Universalium

  • education — /ej oo kay sheuhn/, n. 1. the act or process of imparting or acquiring general knowledge, developing the powers of reasoning and judgment, and generally of preparing oneself or others intellectually for mature life. 2. the act or process of… …   Universalium

  • South Africa — Republic of, a country in S Africa; member of the Commonwealth of Nations until 1961. 42,327,458; 472,000 sq. mi. (1,222,480 sq. km). Capitals: Pretoria and Cape Town. Formerly, Union of South Africa. * * * South Africa Introduction South Africa… …   Universalium

  • steel — steellike, adj. /steel/, n. 1. any of various modified forms of iron, artificially produced, having a carbon content less than that of pig iron and more than that of wrought iron, and having qualities of hardness, elasticity, and strength varying …   Universalium

  • United States — a republic in the N Western Hemisphere comprising 48 conterminous states, the District of Columbia, and Alaska in North America, and Hawaii in the N Pacific. 267,954,767; conterminous United States, 3,022,387 sq. mi. (7,827,982 sq. km); with… …   Universalium

  • metallurgy — metallurgic, metallurgical, adj. metallurgically, adv. metallurgist /met l err jist/ or, esp. Brit., /meuh tal euhr jist/, n. /met l err jee/ or, esp. Brit., /meuh tal euhr jee/, n. 1. the technique or science of working or heating metals so as… …   Universalium

  • Eugenics — is the self direction of human evolution : Logo from the Second International Eugenics Conference, 1921, depicting Eugenics as a tree which unites a variety of different fields.[1] Eugenics is the applied science or the bio social movement which… …   Wikipedia

  • Sarah Keys v. Carolina Coach Company — Sarah Keys v. Carolina Coach Company, 64 MCC 769 (1955) is a landmark civil rights case in the United States in which the Interstate Commerce Commission, in response to a bus segregation complaint filed in 1953 by a Women s Army Corps (WAC)… …   Wikipedia

Share the article and excerpts

Direct link
Do a right-click on the link above
and select “Copy Link”