- Heusler alloy
A Heusler alloy is a
ferromagnetic metal alloy based on a Heusler phase. Heusler phases areintermetallics with particular composition andface-centered cubic crystal structure. They are ferromagnetic even though the constituting elements are not as a result of thedouble-exchange mechanism between neighboring magnetic ions, usuallymanganese which sit at the body centers in a Heusler alloy. The magnetic moment usually resides almost solely on the manganese atom in these alloys. See the Bethe-Slater curve for more info on why this happens.The term is named after a German
mining engineer andchemist Friedrich Heusler , who studied such an alloy in 1903. It contained two partscopper , one part manganese, and one parttin .The Heusler alloy Cu2MnAl has been the subject of a considerable number of studies and the stoichiometric alloy (i.e. one in which the proportion of elements is exactly as in the formula above) has the following properties. It has a room temperature saturation induction of around 8,000 gauss (Bouchard 1970) which is in excess of that of the elementnickel (around 6100 gauss) although less than that ofiron (around 21500 gauss). Early studies (Heusler 1903, Knowlton and Clifford 1912, review Bozorth 1951) showed that the magnetic properties varied considerably with heat treatment and composition. Bradley and Rogers (1934) first showed that the room-temperature ferromagnetic phase was a fully ordered structure of the L21 type. This has a primitive cubic lattice of copper atoms which has alternate cells body-centred bymanganese andaluminium . The lattice parameter is 5.95 angstrom units. The molten alloy has a solidus temperature around 910oC. As it is cooled below this temperature the fully disordered solid body-centred cubic beta phase forms. Below 750oC a B2 ordered lattice forms (Nesterenko 1969, Bouchard 1970) with a primitive cubiccopper lattice body-centred by a disorderedmanganese aluminium sublattice. Cooling below 610oC causes further ordering of the manganese and aluminium sub-lattice to the L21 form (Bouchard 1970, Ohoyama et al 1968). Studies of off-stoichiometric alloys have been made by West and Lloyd-Thomas (1956), Johnston and Hall (1968) and Bouchard (1970). In general the ordering temperatures decrease for these compositions and the range of temperatures within which the alloy can be annealed without forming microprecipitates becomes small.Oxley et al (1963) found a value of 357oC for the Curie temperature, below which the alloy becomes ferromagnetic. A variety of investigators using neutron diffraction and other techniques (e.g. Endo et al 1963, Bouchard 1970) have shown that a magnetic moment of around 3.7 bohr magnetons resides almost solely on the
manganese atoms. As these atoms are 4.2 Angstrom units apart, it seems likely that the exchange interaction aligning the spins must be indirect through conduction electrons or thealuminium and copper atoms. Theoretical studies of the interaction have been made by Oxley et al (1963) and Geldart and Ganguly (1970).Electron microscope studies (Nesterenko 1969, Bouchard 1970) have shown that thermal antiphase boundaries (APBs) form during cooling through the ordering temperatures as ordered domains nucleate at different centres within the crystal lattice and are often out of step with each other where they meet. The anti-phase domains grow as the alloy is annealed. There are two types of APB corresponding to the B2 and L21 types of ordering. APBs also form between
dislocations if the alloy is deformed. At the APB themanganese atoms will be closer than in the bulk of the alloy andelectron microscope studies (Lapworth and Jakubovics 1974) showed that fornon-stoichiometric alloys with an excess ofcopper (e.g. Cu2.2MnAl0.8) anantiferromagnetic layer forms on every thermal APB. Theseantiferromagnetic layers completely supersede the normalmagnetic domain structure and stay with the APBs if they are grown by annealing the alloy. This significantly modifies the magnetic properties of the non-stoichiometric alloy relative to the stoichiometric alloy which has a normal domain structure. Presumably this phenomenon is related to the fact that puremanganese is anantiferromagnet although it is not clear why the effect is not observed in the stoichiometric alloy. Similar effects occur at APBs in the ferromagnetic alloy MnAl at its stoichiometric composition.In recent times, the importance of Heusler alloys for
spintronics has been increasing.Another useful Heusler alloy is the class of materials known as ferromagnetic shape memory alloys which can change their length by up to 10% on application of a magnetic field. These are generally an alloy of nickel-manganese-gallium.
List of Heusler alloys
*Cu2MnAl, Cu2MnIn, Cu2MnSn,
*Ni2MnAl, Ni2MnIn, Ni2MnSn, Ni2MnSb
*Co2MnAl, Co2MnSi, Co2MnGa, Co2MnGe
*Pd2MnAl, Pd2MnIn, Pd2MnSn, Pd2MnSbReferences
* [http://hypertextbook.com/physics/electricity/ferromagnetism/ Ferromagnetism, from The Physics Hypertextbook]
*G. Sauthoff: Intermetallics, Wiley-VCH, Weinheim 1995, S. 83 u. 90.
*cite journal
author= T. Block, M. J. Carey, B. A. Gurney, O. Jepsen
title = Band-structure calculations of the half-metallic ferromagnetism and structural stability of full- and half-Heusler phases
journal = Phys. Rev. B
year = 2004
volume = 70
issue =
pages = 205114
doi = 10.1103/PhysRevB.70.205114
*cite journal
author= Bradley A.J. and Rogers J.W.
title = The Crystal Structure of the Heusler Alloys
journal = Proc. Roy. Soc.
year = 1934
volume = A144
issue = 852
pages = 340–359
url = http://links.jstor.org/sici?sici=0950-1207%2819340329%29144%3A852%3C340%3ATCSOTH%3E2.0.CO%3B2-4
doi = 10.1098/rspa.1934.0053
*cite journal
author= Bouchard M.
title =
journal = Ph.D. Thesis, Imperial College London
year = 1970
volume =
issue =
pages =
*cite journal
author= Bozorth
title =
journal =Ferromagnetism D.Van Nostrand Co.Inc.
year =
volume =
issue =
pages =
*cite journal
author= Endo K., Ohoyama T., and Kimura R.
title =
journal =J.Phys.Soc.Japan
year = 1964
volume = 19
issue =
pages = 1494
*cite journal
author= Geldart D.J.W. and Ganguly P.
title =
journal =Phys.Rev.
year = 1970
volume = B1
issue =
pages = 3101
*cite journal
author= Heusler F.
title =
journal =Verh. Deut. phys. Ges.
year = 1903
volume = 5
issue =
pages = 219
*cite journal
author= Johnston G.B. and Hall E.O.
title =Studies on the Heusler alloys—I. Cu2MnAl and associated structures
journal =J.Phys.Chem.Solids
year = 1968
volume = 29
issue =
pages = 193, 201
doi =10.1016/0022-3697(68)90062-0
*cite journal
author= Knowlton A.A. and Clifford O.C.
title =The Heusler alloys
journal = Trans. Faraday Soc.
year = 1912
volume = 8
issue =
pages = 195–206
doi = 10.1039/TF9120800195
*cite journal
author = Lapworth A.J. and Jakubovics J.P.
title = Effect of antiphase boundaries on the magnetic properties of Cu-Mn-Al Heusler alloys
journal =Phil. Mag
year = 1974
volume = 29
issue =
pages = 253
doi = 10.1080/14786437408213271
*cite journal
author= Nesterenko Y.H.G., Osipenko I.A. and Firstov S.A.
title =
journal =Fiz.Metal.Metalloved.
year = 1969
volume = 27
issue =
pages = 135
*cite journal
author= Ohoyama T., Webster P.J. and Williams K.C.
title =
journal =J.Appl.Phys.(D)
year = 1963
volume = 1
issue =
pages = 951
*cite journal
author= Oxley D.P., Tebble R.S. and Williams K.C.
title =Heusler Alloys
journal =J.Appl.Phys.
year = 1963
volume = 34
issue =
pages = 1362
doi =10.1063/1.1729511
*cite journal
author= PJ Webster
title = Heusler alloys
journal = Contemporary Physics
year = 1969
volume = 10
issue = 6
pages = 559–577
doi = 10.1080/00107516908204800
*cite journal
author= West D.R.F. and Lloyd Thomas D.
title =
journal =J.Inst.Met.
year = 1956
volume = 85
issue =
pages = 97External links
* [http://www.npi.gov.au/database/substance-info/profiles/27.html National Pollutant Inventory - Copper and compounds fact sheet]
Wikimedia Foundation. 2010.