- Tooth Interior Fatigue Fracture
Tooth Interior Fatigue Fracture, (TIFF), is a type of
gear failure. The failure is characterised by afracture at approximately mid-height on the tooth of the gear. This distinguishes it from a tooth root fatigue failure. The crack for a TIFF is initiated in the interior of the tooth. This distinguishes TIFF from other fatigue failures of gears. TIFF has been observed in case-hardenedidler s (i.e. gear wheels loaded on both flanks during each revolution).The TIFF fracture surface has a distinct plateau in the central part along the tooth width and approximately mid-height of the tooth. In a close-up of the cross-section of the TIFF small wing cracks are observed. The presence of the wing crack indicates that the main crack has propagated from the centre of the tooth toward the tooth flank.
The crack-producing stresses of TIFF are twofold: i) constant residual tensile stresses in the interior of the tooth due to case hardening; and ii) alternating stresses due to the idler usage of the gear wheel.
Contact fatigue begins with surface distress, which can grow to
spalling . In severe cases a secondary crack can grow from a spalling crater through the tooth thickness and a part of the tooth can fall off. In contrast to the fracture of severe contact fatigue, spalling craters are not necessary at the flank surface for a TIFF.ee also
Fracture mechanics References
* cite journal
last = MackAldener
first = Magnus
authorlink =
coauthors = Mårten Olsson
title = Interior Fatigue Fracture of Gear Teeth
journal = Fatigue and Fracture of Engineering Materials and Structures
volume = 23
issue = 18
pages = 283-292
publisher =
location =
date = 2000
url =
doi =
id =
accessdate =* cite journal
last = MackAldener
first = Magnus
authorlink =
coauthors = Mårten Olsson
title = Analysis of crack propagation during tooth interior fatigue fracture
journal = Engineering Fracture Mechanics
volume = 69
issue = 18
pages = 2147-2162
publisher = Elsevier Science Ltd.
location =
date = December 2002
url =
doi = 10.1016/S0013-7944(02)00016-4
id =
accessdate =
Wikimedia Foundation. 2010.